大体积混凝土结构表面保温措施工程实例分析

资料大小：450KB
资料类型：.PDF
资料等级：
发布时间：2022-07-03

资料介绍

摘要：为了避免某水电站坝体在施工和薪水运行过程中因温度应力超过混凝土抗拉强度而产生裂缝,结合该大坝
的实际工程将大业有限件ANSYS与=维有限元退体程序RCTS 相结合计访水圳体车
线方向楼绛之间的整股市期和运行期的湘度场，货力进行了方直计算计算结果专用：项体基础常杰混
场十热层部位在外湘专化及基岩约束双币作用下，出现了较大的拉应力。混凝十表面铺设保温板后,减小了外界涓
度对混凝十的影响,垫层部位的最大应力有所降低见，混凝十麦面铺设保温板是降低温度应力的有效措施。
关键词:大体积混凝土；重力坝;表面保温；温度场；温度应力
中图分类号：TV43I；TV523
文献标识码：A
Case study of insulation measures for the surface of mass concrete structure
LEI Yan',ZHAO Li juan', ZHOU We?
(1.Hydrochina Xibei Engineering Corporation,CHECC, Xian 710065, China；
2. Sichuan Daduhe Shuangjiangkou Hydropower Project Development Company Lid.,Maerkang 624000, China)
Abstract:To prevent the dam of a hydropower station firom cracking duerature stress lan concrete tensile during
dam constnuction and impoundment, this paper , based on the actual operation conditions of the dam and by combiming the large commer-
cial FEM software ANSYS with the 3D FEM temperature control progme RCTS. carries out simulation calculation of the temperatur
feld and stress of the dam block between the latitudinal jong the dam axis direction in the constructioperation peri-
ods. The calculation result shows that the normal concrete cushion of dam foumdation has great tensile stress under the double action of ex-
ternal temperature chand bedrock constraingulation boaid ower the concrete reduce the induermal
perature stress is to lation boards ovete surface.
Key words:mass concrete；gTavity dam；surfacc insulation；temperature field；temperature stress
0 引言
减少结构的裂缝,从而提高混凝土的抗渗、抗裂、抗
侵蚀性能和耐久性是极其重要的11-71。
。实践经验证
工程实例证明,大体积混凝土产生的裂缝大多
明,在大体积混凝土表面铺设保温板是一种有效的
都是在浇筑过程中由于温度变化而引起的。气温骤
温控防裂措施,尤其是对于高寒地区以及受寒潮作
降引起混凝土内外温度梯度过大而产生很大的拉应
用的大体积混凝土建筑物效果十分明显。本文结合
力,这些温度应力是产生表面裂缝的主要原因。因
某严寒地区碾压混凝土重力坝工程,用等效表面散
此,对大体积混凝土而言,控制其温度应力,防止和
热系数法计算分析了无保温板和有保温板条件下坝
体的温度场、温度应力场,进一步证明了大体积混凝
收稿日期：2010-09-26
土表面铺设保温板对于防止表面裂缝的有效性。