：介绍了混凝土微胶囊自修复技术的机理，选用原位聚合法制备脲醛树脂包覆的环氧树脂微胶囊，并通过在混凝土中掺入该 微胶囊制得 自修复混凝土。通过研究微胶囊对混凝土强度和工作性的影响，确定了微胶囊适宜掺量为 3．O％，评价 了 自修复混凝土对 受 载损伤和环境损伤 的修复性 能：受载损伤后 48h的抗折强度恢复率为 75．6％，冻融循环实验后动弹性模量平均恢复率可达 64．3％。 关键词 ：混凝土；损伤；自修复；微胶囊；耐久性 ‘ 中图分类号 ：TU528 文献标识码 ：A 文章编号：1001—702X(2014)05—0040—03 Experimentalstudy and evaluation ofserf healing concrete th encapsulated glue N 帆 ， N Chao (DepartmentofCivilEngineering，Sichuan College ofArchitecturalTechnology，Deyang 618000，Sichuan，China) Abstract：The mechanism of selfhealing technology for concretewas introduced．A kind ofepoxy resin microeapsule with ureaformaldehyderesin coatwasprepared by the method ofin situ condensation polymerization，and theselfhealingconcrete was prepared by adding this microeapsule．The microcapsule appropriate content 3．0％ was determined according to the influence of microeapsule on concrete pmpe~ies． Recovering perform an ce of self healing concrete for the loading damage and environmental damagewasevaluated：afterloading 48h。the recovery rate ofthe flexuralstrength was75．6％ ：withstanding freeze—thaw cycles，the averagerecoveryrate ofmodulusdynamicupto 64_3％． Key words：concrete：dhmage：selfhealing：miemcapsule：durability 在载荷作用、环境侵蚀等多种因素的影响下，混凝土结构 经常出现裂缝等局部损伤。混凝土开裂减小了结构的承力面 积，使结构的强度下降。另外，裂缝会成为环境中的腐蚀物质 渗透进入混凝土内部的通道，加速混凝土及钢筋的腐蚀，导致 结构的耐久性降低Ill。对于结构表面的宏观裂缝，通常可以采 取加固、灌浆、填充等人工修复方法田。而结构内部裂缝以及 微观开裂则不仅不易检测到而且难以用传统修复方式处理。 混凝土自修复就是指混凝土在开裂时能够自行感应并修复损 伤的新型技术[31。本文利用掺加修复微胶囊来实现混凝土的 自修复，对其性能进行了实验研究，并评价了自修复的效果。 1 微胶囊自修复机理 复剂的微胶囊来实现，其自修复机理如图1所示。当混凝土基 体开裂时，微胶囊随之破坏，其中的修复剂流出，并在毛细作 用下渗入裂缝。修复剂固化后将断裂面粘结在一起

因本站资料资源较多，启用了多个文件服务器，如果浏览器下载较慢，请调用迅雷下载，特别是超过了5M以上的文件！请一定调用迅雷，有时候速度就会飞起哦，如果您的浏览器自动加载了PDF预览，文件太大又卡死，请按下载说明里的把PDF插件关闭了就可以直接下载，不会再预览了！