微波蒸压技术快速养护加气混凝土砌块试验研究

资料大小：500KB
资料类型：.PDF
资料等级：
发布时间：2022-05-05

资料介绍

摘要：为了加速养护加气混凝土物块，骋撒波技术应用到传统的燕压养护工艺中，设计和制作了小型微波燕
压荟，并采用试验釜开展了一系列的试验研完。研究姑果表明，当微波加热时间在20m,恒温时间44.5h,恒温温
度180-190℃，降温时间1h,加气混凝土强度满足出釜强度3.0MPa、密度等级683813水g/m的质量控制要求。
关键词：微波：燕压东护：加气混凝土砌块：养护制度
Abstract:In order to cure aerated conerete block quickly,mierowave was applied to the conditional autoclave curing.
A small microwave autoclave was designed and made,and a series of experimental studies were conducted with small mi-
crowave autoclave.The results show that when the microwave heating time is 20min,the constant time is 4-4.5h.the con-
stant temperature is 180-190C.and the cooling time is Ih,the strength of aerated concrete block ean meet the quality
control requirements that the strength of aerated concrete out of the autoclave is 3.0MPa,and the density rank is in the
range of 683-813kg/m'.
Key words:Microwave:Autoclave curing:Aerated concrete block:Curing system
中图分类号：TU522.3
文献标识码：A文章编号：1000-4637(2015)05-62-03
0前言
试验所用加气混凝土砌块全部采用某企业生
目前，加气混凝土砌块在墙材中占据重要地
产时所用的B06级配料，砌块尺寸为200mm×
位，作为传统墙材的替代产品，具有质轻、保温（隔
200mm×600mm和100mm×200mm×600mm两种，以
热)、利废、抗火、抗震、施工方便等优点4。现行的
该厂质量控制出釜强度3.0MPa、密度等级683-
粉煤灰（砂）加气混凝土砌块采用蒸压釜进行高温
813kgm3和出釜含水率28%-30%为合格标准。
高压养护，高温蒸汽通过热传导将热量由表及里传
1.2
试验方法
递给被养护砌块，砌块内部存在较大的温度梯度，
自行设计和制作了一台微波蒸压试验釜，如图
温度场极不均匀，因而现行加气混凝土砌块养护制
1所示，并采用试验釜开展了系列的试验研究。微波
度大多历时较长（一个周期约10h),原因在于升、降
蒸压试验釜采用与传统蒸压釜相同的结构、构造，
温速度不能快（因而升、降温时间较长），否则太大
为钢制卧式筒型结构，釜体为16MnR钢筒，直径
的温度梯度将会引发较大的温度应力，导致被养护
800mm,壁厚10mm,长1200mm,侧开釜门：设计温
砌块的坯体开裂、强度降低，成品率下降。
度190℃，压力1.4MPa。
微波加热具有升温速度快、温度场均匀的显著
优势，将微波发生器安装到传统蒸压釜上，在蒸压
釜升温阶段结合高强度的微波照射砌块，将在砌块
内形成比较均匀的温度场，砌块温度表里如一，同
步升温，即使在恒温阶段，砌块内部极为均匀的温
度状态，对其强度的发展将极为有利，采用这一创
新工艺后州，必将大幅缩短现行的加气混凝土砌块
生产周期、降低能耗。
1试验概况
图1小型微波蒸压试验釜
1.1试验材料
试验按GB/T11969-2008《蒸压加气混凝土性