摘要：为研究喷涂混凝土夹心剪力墙的轴心受压承载力，完成了4个试件的轴心受压试验。试验结果表
明：试件破坏形态为弯折破坏：夹心墙的轴心受正承载力可采用钢筋混凝土柱轴心受压承裁力的计算公式进行
计算。
关键词：喷涂混凝土；夹心墙：轴心受压承载力：静力试验
中图分类号：U317.1
文献标识码：A
文章编号：10004726(2013)11-1021-03
TEST STUDY ON AXIAL COMPRESSIVE STRENGTH OF
SPRAYED CONCRETE SANDWICH WALLS
SONG Xiao-lu',QIAN Jia-ru'.FENG Bao-chun*,ZHANG Yi-chao?
(1.Key Laborstory of Civil Ergineering Safety and Durability of China Educstion Ministry.
Department f Civil Engineering.Tsinghun University,100084.Beijing.China;
2.Beijing Hua Mei Ke Bo Science and Technology Development Co.,Ld10007,Beijing.China)
Abstract:To study the axial compressive strength of the sprayed concrete sandwich walls,static tests of 4
specimens were carried out.The results indicated that the failure mode of specimens was bending broken of wall
panel.The axial compressive strength of the sprayed concrete sandwich wall can be calculated by using the
code formula which is used to calculate the axial compressive strength of reinforced concrete columns.
Key words:sprayed concrete;sandwich wall;axial compressive strength;static test
夹模喷涂混凝土夹心剪力墙结构是一种新型建筑
两端分别浇筑钢筋混凝土底梁和顶梁；试件的保温板
结构体系，其主要承重和抗侧力竖向结构构件为夹模
厚度为60mm:试件1,2为单层钢网夹心板，两表面各喷
喷涂混凝土夹心剪力墙。喷涂混凝土夹心剪力墙（以下
涂50mm厚混凝土，总厚160mm:试件3,4为双层钢网夹
简称“夹心培")采用工厂制作的标准化双层钢丝网架
心板，两外表面喷涂50mm厚混凝土，两层钢网夹心板
聚苯夹心板（以下简称“钢网夹心板”），通过专用夹模
间距100mm,配置钢筋网，钢筋直径6mm、间距150
固定，喷涂钢网夹心板面层混凝土，成为喷涂混凝土夹
mm,后浇混凝土，试件总厚为320mm。试件尺寸及构造
心剪力墙：后浇筑夹心剪力墙两端的混凝土柱，形成带
如图1所示。
现浇端柱的夹心剪力墙。
钢丝网采用3钢丝，双向间距均为50mm,钢丝网
夹模喷涂混凝土夹心剪力墙与楼层标高位置的现
由自动化钢网夹心板平网焊接设备焊接成型：铜丝网
德圈架、楼盖（屋盖）一起，构成承重和杭侧力结构体
与60mm厚聚苯板一起进入全自动钢网夹心板插丝焊
系，具有节材、保温隔热、隔声和防火等优良性能，在多
接机，插丝也采用03钢丝，间距100mm或200mm,插丝
层住宅建筑中具有广阔的应用前景。
与两则钢丝自动焊接，连接聚苯板两侧钢丝网，成为双
为研究喷涂混凝土夹心剪力墙的轴心受压承载
层钢网夹心板。
力，为工程设计计算夹心墙的轴压比提供科学依据，完
1.2材料强度
成了4块夹心墙的轴心受压试验。
1.21钢丝和钢筋
3钢丝的实测屈服强度和极限强度分别为
1试验概况
626.8MPa和709.6MPa,6钢筋的实测屈服强度和极限
1.1试件
强度分别为365.8MPa和524.8MPao
4个夹心墙试件的墙高为2400mm、宽为550mm,
1.2.2混凝土