利用废弃泡沫玻璃边角料为原料，设计了3组不同颗粒级配的泡沫玻璃，制备出泡沫玻璃保温混凝土，对其力学强度与 保温性 能进行 了测试和微观结构分析 。结果表 明，泡沫玻璃保温混凝土所用 的骨料 颗粒越小，颗粒之 间粘 结效 果越好，抗压强度较 高 ，导热系数也更低 。 关键词 ：泡沫玻璃；颗粒级配：抗压强度；导热系数 中图分类号 ：TU551．33 文献标识码 ：A 文章编号 ：1001—702X(2014)06—0076—04 Experimentalstudy oilthe influence of foam glass particle gradation on the strength and insulation properties of therm alins~afion concrete LIU Yingying，XIONG Houren，WUHaidong，WANG Qinglgo,YU Ge (InstituteofBuildingEnergyResearch，JiaxingUniversity，Jiaxing314001，Zhejiang，China) Abstract：Inthispaper，byusingwaste foam gla~sleftovermaterial，threegroupsoffoam glasswith differentparticle size distribution were designed，and foam glass insulation concrete was prepared．The mechanical strength an d heat preservation perfor- mance offoam gla~sinsulationconcretewere tested and microstructurewasanalyzed．Experimental resultsshow thatthesmaller the aggregate particles used forfoam glassinsulation concrete，the betterthe bonding efectbetween particles，the higherthe corn— pressivestrength，and the lowerthethermal conductivity． Key words．foam glass；srain sizedistribution；compressive strength；therm al conductivity 0 引 言 泡沫玻璃是一种以废弃玻璃为原料制各的新型保温材 料，它集保温隔热、防火、防水、隔声、吸声、轻质、无毒无害等 优点于一体，是高性能建筑保温材料的代表[1j。将泡沫玻璃添 加到混凝土中，代替混凝土中的部分骨料用于外墙保温，能 充分发挥泡沫玻璃的保温性能。 本研究以废弃泡沫玻璃边角料为原料，代替部分混凝土 基金项 目：嘉兴市科技计划项 目(2012AY1018)： 浙江省教育厅资助项 目(Y201226031)： 浙江省大学生科技创新活动计划 (新苗计划)资助项 目 (2013R417026)： 嘉兴学 院校级重点课题资助项 目(7011001IBL) 收稿 日期：2013—01—24 作者简介：刘莹莹 ，女 ，1991年生，吉林舒兰人，通讯作者：熊厚仁 ，E— mail：】O40720o5@ 】63 。 ·76· 新型建筑材料 2014．6 骨料，制成泡沫玻璃保温混凝土。试验设计了3组不同颗粒级 配的泡沫玻璃保温混凝土，研究了颗粒级配对泡沫玻璃保温混 凝土强度及保温性能的影响。确定了既满足混凝土的物理力 学性能，同时又满足保温性能的最佳泡沫玻璃的颗粒级配[21， 使得混凝土在浇筑成建筑物外围护结构构件时，既可以承受 建筑物荷载，又能解决建筑物节能保温问题，以达到节约资源 的目的。 1 试 验 1．1 原料 (1)废弃泡沫玻璃边角料，堆积密度为 150—170kg／m3，浙 江振申绝热科技有限公司生产，现场筛选3组不同级配范围 的泡沫玻璃颗粒分别为 l6．00～9．50mm、9．504．75mm、4．75— 2．36mm，泡沫玻璃原料照片如图1所示。 (2)水泥：P·S42．5普通硅酸盐水泥： (3)水：自来水。 1．2 试验过程

因本站资料资源较多，启用了多个文件服务器，如果浏览器下载较慢，请调用迅雷下载，特别是超过了5M以上的文件！请一定调用迅雷，有时候速度就会飞起哦，如果您的浏览器自动加载了PDF预览，文件太大又卡死，请按下载说明里的把PDF插件关闭了就可以直接下载，不会再预览了！