硫酸盐浸烘腐蚀淡化海砂混凝土的试验研究

资料大小：780KB
资料类型：.PDF
资料等级：
发布时间：2022-03-26

资料介绍

摘要：对淡化海砂混凝土在5%Na,SO（质量分数，下同）.5% MgSO，3.5% NaCl两种腐蚀溶液中干湿循环的损
伤过程进行研究。结果表明；Na,SO。溶液浸烘循环中,混凝土的损伤表现为动弹性模量先下降后上升最后加速下
降;腐蚀溶液中Mg*与SO2 共同作用下,混凝土的损伤表现为动弹性模量随腐蚀时间先降低,后稳定发展,即将
破坏时迅速下降。
关键词：硫酸盐腐蚀；淡化海砂；干湿交替；动弹模
中图分类号：TU528
文献标志码:A
文章编号：1008 - 1933（2013）04 - 239 -04
Study the corrosion of drying-wetting sulfates on washed
sea sand concrete
SU Qing',CHEN Airong',ZHAO Tiejun'
(1. Department of Bridge Engineering,Tongji University,Shanghai 200092,China;
2.School of Civil Engineering,Qingdao Technological University,Qingdao 266033,China)
Abstract;The damnge process and mierostructure of washed sea sand concrete, ,attacked by solutions of 5% Na,SO,(by mass, Bame
below),5% Mgso,+3.5% NaCl with method of drying-wetting cycle are studied. The results show that the elastie modulus of concrete
attacked by Na,so,behavions in a decreasing stage followed by improved stage finally fell rapidly.For the concre
composed of Mg** and sot , ,its relative dynamic elastic modulus decreased finstly,then kept stable,finally decreased napidly to failure.
Key words:sulfate comosion;washed sea sand;drying-weiting cycle;dynamic elastic modulus
0 前言
我国沿海地区海砂资源丰富,偷采海砂现象严
重。20 世纪80年代,由于滥用海砂致使以“海砂
屋"为代表的海砂建筑腐蚀问题频额出现,工程界
谈海砂而色变。近年来,以宁波、舟山为代表的沿海
城市,逐渐形成了具有一定规模的海砂开采产业
（图1），且海砂产量巨大,在建筑砂市场上占据相当
大的份额。据不完全统计[12]
,2003年我国海砂开
采约9000 多万吨,产值达22.5亿元。因此,利用淡
(a)采砂设备
化海砂为缓解建筑砂供求矛盾提供了新的途径。
沿海地区，盐类腐蚀是引起混凝土结构物性能
劣化的主要元凶。虽然海域不同,但海水的平均含
盐量约为35g/1,主要是氯盐、硫酸盐和镁盐。由于
氯盐侵蚀是引起钢筋锈蚀的主要原因,因此针对海