可泵送免压蒸C80PHC混凝土制备、养护与性能研究

资料大小：450KB
资料类型：.PDF
资料等级：
发布时间：2022-03-15

资料介绍

：以超细粉煤灰为免压蒸混凝土掺合料，研究其掺量对混凝土流动性能、力学性能的影响。结果表明，超
细粉煤灰掺量低于 16％时．混凝土坍落度、脱模强度与其掺量正相关；掺量大于 16％时，对其流动性、脱模强度影响
不大，甚至降低；掺入超细粉煤灰，混凝土拉压比提高，脆性降低。所研制的 C80PHC 混凝土坍落度达 150turn，经蒸
汽养护(匀速升温 2h、恒温 5h、降温 1h，恒温温度 85℃ )后脱模强度达到 79．4MPa，28d抗压强度达到 87．4MPa。
关键词：免压蒸养护；超细粉煤灰；养护制度；经济性
Abstract：Ultra—fine fly ash was utilized as the admixture of concrete by non—autoclaved curing．The fluidity and
mechanical properties of concrete were investigated with different dosages of ultra—fine fly ash．The results show that the
slump and demoulding strength of concrete are in a positive correlation with the dosage of ultra—fine fly ash lower than
16％． e slump and demoulding strength rarely increase or even decrease a little when the dosage exceeding 16％． rhe
tensile／compressive strength ratio increases with fly ash due to a reduction in brittleness．The demoulding strength and 28d
strength of C80PHC concrete with a slump of 150ram reach to 79．4MPa and 87．4MPa respectively after a steaming curing
(uniform raising temperature for 2h，constant temperature of 85℃ for 5h，lowering temperature for lh)．
Key words：Non—autoclaved curing；Ultra-fine fly ash；Curing regime；Economy
中图分类号：TU528．01 文献标识码：A 文章编号：1000—4637(2015)O3—21—07
0 前言
PHC管桩是一种重要的桩基材料．将其应用于
桩基础可缩短建设周期，同时节约大量能源。因而
在建筑业得到广泛应用。随着基础建设的发展，
PHC 管桩产量迅速增大_l-2]。目前，管桩厂多使用磨
细砂作为掺合料，利用高温高压条件生成结构稳定
的托贝莫来石，从而加快混凝土内部结构的形成。
然而，掺人大量磨细砂的同时，会带来混凝土流动
性低、保水性能差、养护时间长等问题：采用高温高
压蒸汽养护不仅投人成本提高、能耗增加，同时也
造成 PHC混凝土内部晶体结构中粗大晶粒多，晶胶
比偏大【31，混凝土桩身脆性大等问题。因此，亟需从
技术手段上解决 PHC管桩混凝土生产的问题，以期
达到降低能耗、减少投入成本，同时提高 PHC管桩
混凝土各项性能的目的。
以超细粉煤灰为掺合料，利用其形态效应、微
集料效应[4】。降低混凝土需水量、提高混凝土保水性
和密实度；并采用一次蒸汽养护、水泥水化产物 Ca
fOH) 碱激发剂双重作用发挥超细粉煤灰火山灰活
性[5]，研制出可泵送免压蒸的 CSOPHC混凝土。本文
研究了超细粉煤灰掺量 (0、8％、16％、24％、32％)对
混凝土流动性能、力学性能的影响，从而为混凝土
配合比的优化提供理论基础，在最佳配合比基础上
研究混凝土在恒定养护温度 85℃ ，不同恒温时间
(1h、3h、5h、7h、9h、1lh)下的脱模强度，以期获得混
凝土的最佳恒温养护时间。
1 试验
1．1 原材料
水泥：P·Ⅱ42．5R 型水泥，其物理性能见表 l；
砂：江砂，其性能见表 2；石：花岗岩，按大石：小石 =
2．5：1混合，其性能见表 3：超细粉煤灰：物理性能见
表 4，粒度分布见图 1；减水剂：聚羧酸高性能减水