静载和疲劳荷载作用下环氧涂层钢筋混凝土梁的耐久性能

资料大小：450KB
资料类型：.PDF
资料等级：
发布时间：2022-03-13

资料介绍

：对三组钢筋混凝土梁在外荷载和服役环境下的耐久性能进行了试验室模拟研究。运用电化学方法对试
件中不同涂层钢筋和无涂层钢筋的阻抗进行了测试和等效电路模拟，结合不同试件的裂缝分布，对模拟结果进行了
分析。结果表明，环氧涂层能提高钢筋的耐腐蚀性；加载彤式不同会对试件钢筋锈蚀产生不同影响；随盐水腐蚀时间
的增加．试件中不同厚度涂层钢筋的抗锈蚀能力也有不同程度的退化。
关键词：环氧涂层；耐久性；静栽；疲劳荷载；环境腐蚀
Abstract：Laboratory simulation research on the durability behaviour of the three groups of reinforced concrete(RC)
beams external load and environment attacks was studied，test and equivalent circuits modeling of impedance for specimen
containing different epoxy—coated reinforcing bar and uncoated reinforcing bars by using electrochemical method are carried out。that simulation results aye analyzed by combining with cracks distribution of difierent specimens．The results show
that，epoxy coating can provide effective anti-corrosion protection for the reinforcing bars；the corrosion of the reinforcing
bars in RC test specimens is influenced by external load．Deterioration of the anti～corrosion protection for reinforcing bars
with difierent coating thicknesses in test specimens is shown with the increase of the simulated seawater solution attack．
Key words：Epoxy coating；Durability；Static load；Fatigue load；Environmental attack
中图分类号：TU511．32 文献标识码：A 文章编号：1000—4637(2016)04—78—07
0 前言
为解决服役钢筋混凝土构件和结构中钢筋的
锈蚀问题，一个切实有效的方法是采用环氧涂层钢
筋[1]。目前，国内外对环氧涂层钢筋混凝土试件力学
性能的试验研究和环氧涂层钢筋耐腐蚀性的研究
较多．但是对于疲劳荷载和环境腐蚀两者共同作
用下环氧涂层钢筋混凝土的研究则未涉及。实际服
役情况下，大部分的钢筋混凝土构件均带裂缝工
作，这些荷载产生的裂缝为服役环境中有害介质的
侵入提供了有利的渠道，使得带裂缝混凝土中有害
介质 (氯离子 )到达钢筋表面的时间大大缩短凹；另
一方面，环氧涂层钢筋能充分隔断造成钢筋腐蚀的
三种因子(水、氧、腐蚀性离子 )的传输过程。但较厚
的涂层使钢筋与混凝土间黏结强度降低较大翻，使
得构件中出现较宽的裂缝，从而加剧钢筋锈蚀。 ·
试验采用普通无涂层、0．2ram涂层和 0．6rnm厚
涂层的钢筋混凝土试件。先对试件进行了静力加载
和疲劳加载，再对加载后试件和未加载试件进行了
3％ 5％的模拟盐水腐蚀。对经历一定干湿循环的试
基金项目：国家自然科学基金项目(51178266)。
一 78一
件中钢筋的阻抗进行了电化学测试，并对测试结果
进行了等效电路模拟分析：根据测试和模拟结果分
析了加载情况及涂层厚度对试件耐久性能的影响。
1 试验简介
1．1 试件
钢筋混凝土试件截面尺寸为 120mmx300mm，
全长 1．5m，见图 1，纵向受力钢筋为 3根直径为
12mm的 Ⅱ级钢筋。纵向钢筋的底边混凝土净保护
层厚度为 40mm，侧边 60mm；箍筋为直径 8mm的Ⅲ
级钢筋，混凝土设计强度等级 C40，水胶比 O．44。
按图 1绑扎钢筋笼。其中钢筋的位置标注如图