：对内掺有机硅防水剂制备的整体防水混凝土进行抗水冻、盐冻试验，通过相对动弹模量和质量损失率，定量分析
其在冻融环境下的耐久性。结果表明，内掺有机硅防水剂的混凝土在水冻、盐冻环境下，抗冻性较未经整体防水处理的
空白混凝土试件差，并且随着有机硅防水剂掺量的增加，混凝土劣化速率加快。
关键词 ：整体防水混凝土；有机硅防水剂；抗冻·li；质量损失
文章编 号 ：l0o7-497X(2013)一08—0019—04 中图分类号 ：TU528．042+．6 文献标识码 ：A
Study on W ater Freeze Resistance‘and Salt Freeze Resistance of
Integral W aterproofing Concrete
Ma Zhiming ，Zhao Tiejun ，Chen Jizhou ，Guan Ting
(1．School of Civil Engineering，Qingdao Technological University，Qingdao，Shandong 266033，China；
2．Qingdao Municipal Group Concrete Industry Engineering Co．，Ltd．，Qingdao，Shandong 266033，China)
Abstract：W ater freeze resistance and salt~eeze resistance of integral waterproofing concrete with organosilicon waterproofing
agent were tested，and the durability of the integral waterproofing concrete under freeze—thaw environment was quantitative
analysed by relative dynamic modulus and mass loss．The results showed that frost-resistance of concrete with organosilicon
waterp roofing agent was weaker than that of blank concrete sample under water freeze and salt freeze environment，and the
degradation accelerated with the increase of the dosage of organ osilicon waterproofing agent．
Key words：integral waterp roofing concrete；organosilicon waterp roofing agent；anti-freeze；mass loss
耐久性不足是混凝土结构达不到设计使用寿命
的主要原因之一[1】，而水分及有害物质 的侵人又是混
凝土结构发生劣化 的重要条件 ，故对混凝土进行防水
收稿 日期 ：2012—11-22
基金项目：973项 目，编号 2009CB623203。
作者简介：马志鸣，男，1987年生，青岛理工大学结构工程在读
硕士研究生 ，研 究方向为混凝土耐久性。联 系方式 ：266033山
东省青岛市四方区抚顺路 11号青岛理工大学研 10级 1班。
处理是提高其结构耐久 陛、延长使用寿命 的有效可行
手段。研究表明 ，在未受损伤的情况下 ，内掺有机硅防
水剂制备的整体防水混凝土 ，具有 良好的抵抗水分和
氯离子侵入的能力[2-31。但是，目前还未见对内掺有机
硅防水剂的整体防水混凝土在冻融环境下进行抗冻
性研究的报道 。
本研究制备了整体防水混凝土试件，其中，有机
硅防水剂的掺量分别为 0％、2％和 4％(相对于水泥的