采用热激活法对造纸白泥一页岩一煤矸石进行改性，开发出一种新型混凝土掺合料，并研究了其对混凝土性能的影响。结果表明， 新型掺合料在混凝土 中掺量为 20％ 时，未对混凝土早期力学性能产生 负面影响，后期强度还较基准试样有一定程度提 高。新型掺合料混凝土具有 较好的减水剂适应性和耐久性。 关键词 造纸白泥 混凝土掺合料 页岩 煤矸石 中图分类号 ：TU528．041；X793 文献标识码 ：A StudyonConcreteAdmixtureProducedbyLimeM ud，ShaleandCoalGangueasRaw M aterials LiuZheyi LiuLaibao XuGuangliang ZhangLihua LiHao (StateKeyLaboratoryCultivationBaseforNonmetalCompositesandFunctionalMaterials，SouthwestUniversityofScienceandTechnology,Mianyang， Sichuan 621010) Abstract A new typeofconcreteadmixturewasmanufacturedbylimemud，shaleandcoalganguethroughthermalactivation．Theimpactof thenew concreteadmixtureonthepropertiesofconcretewasstudied．Theresultsshowedthat theoptimalratioofsubstitutedcementdosagewas20％， therewasnonegativeeffectsOn theearly age mechanicalbehavioroftheconcreteby adding into thisnew adm ixture，and them echanicals~ength hadbeenimprovedatthelateragecomparedwithonewithoutadm ixture．Theconcretemadebythisnew adm ixturehasgoodadaptability with water reducingagentan dgooddurability． Keywords limemud concreteadm ixture shale coalgangue 造纸 白泥是造纸厂碱 回收过程 中得 到含水率 25％-60％ 的废弃沉淀物。随着我国制浆造纸企业新 建的碱回收系统数量增多、规模扩大，产生的造纸自 泥将大幅增加并积累，全部厂外排放会造成严重的环 境污染 [1]。由于技术、经济等原 因，在造纸白泥综合 利用中面临很多问题 [2刊，因此造纸白泥的处理及资 源化利用问题迫在眉睫。页岩是以氧化硅和氧化铝 为主要成分的黏土质沉积岩 ，通常其晶体结构非常稳 定，几乎无活性，但在一定温度下煅烧后可产生晶体 缺陷从而激发其活性 。页岩储量大，开采方便 ，可 广泛应用于建材行业。煤矸石是我国排放量最大的 固体废弃物。水泥混凝土能有效固化有害组分，是消 纳处理各种废物 的有效途径 [8]。．本实验采用热激活 法对造纸白泥 一页岩一煤矸石进行改性，开发出一种 新型混凝土掺合料，并进一步研究其对混凝土的工作 性、力学性能和耐久性的影响，为废弃物资源化应用 于混凝土提供理论指导。 1 实验部分 1．1 原料 竹浆造 纸自泥，含水率 46％，四川 安县 收 稿 日期 ：2013-09—21 基金项 目：国家科技 支撑计划项 目(2011BAA04B04)；四川省教育 厅科研重点项 目fl1ZD1002)。 一 18 ．纸业有限公 司；页岩，四川安县；煤矸石，四川绵竹； P·042．5型水泥，~ll'JII中联产。页岩与煤矸石为块状， 试验前将其破碎再入球磨机粉磨 30min，细度达到 80pm方孔筛筛余小于 6％作为原料使用。原料的化 学组成见表 1。造纸白泥 XRD、差热分析、粒度分析 及 SEM 形貌图，分别见 图 1、图 2、图 3、图 4，页岩及 煤矸石 XRD分析见图 5。

因本站资料资源较多，启用了多个文件服务器，如果浏览器下载较慢，请调用迅雷下载，特别是超过了5M以上的文件！请一定调用迅雷，有时候速度就会飞起哦，如果您的浏览器自动加载了PDF预览，文件太大又卡死，请按下载说明里的把PDF插件关闭了就可以直接下载，不会再预览了！