再生混凝土中氯离子渗透性能试验研究

资料大小：330KB
资料类型：.PDF
资料等级：
发布时间：2021-10-29

资料介绍

：通过氯离子自然扩散试验，测定再生混凝土试件中的氯离子浓度，分析了再生骨料、粉煤灰
掺量、全浸泡与干湿循环方式对再生混凝土中氯离子渗透性能的影响．结果表明：再生混凝土抗氯
离子渗透能力比普通混凝土差；掺入粉煤灰能提高再生混凝土抗氯离子渗透能力，粉煤灰最佳掺
量为 2O (质量分数 )；干湿循环方式可加快再生混凝土中氯离子的渗透速度．
关键词：再生混凝土；氯离子；渗透；干湿循环；粉煤灰
中图分类号：TU528．01 文献标志码：A doi：10．3969／j．issn．1007—9629．2011．03．018
Experim ental Study on Chloride Ion Penetration into Recycled
Aggregate Concrete
Xiang—hao， YUE Peng-jun
(School of M arine Environment and Engineering，Shanghai M aritime University，Shanghai 201306，China)
Abstract：In order to investigate the effects of recycled concrete aggregate，wet and dry cycles，fly ash re—
placement on chloride ion penetration of recycled aggregate concrete，the chloride ion concentration in re—
cycled aggregate concrete was measured during chloride natural diffusion test．The results show that the a—
bility to resist chloride ion penetrate into recycled aggregate concrete is weaker than that for natural aggre—
gate concrete；the resistance to chloride ion penetration into recycled aggregate concrete can be improved
by replacing cement with fly ash，20 (by m ass)replacement of cement with fly ash is optimum ；the rate
of chloride ion penetration into recycled aggregate concrete under wet and dry cycles is higher than that into
saturated recycled aggregate concrete．
Key words：recycled aggregate concrete；chloride ion；penetrate；wet and dry cycle；fly ash
再生混凝土是用再生骨料部分或全部替代天然
骨料拌制的一种新型生态混凝土，与天然骨料相比，
再生骨料的孔隙率大，导致再生混凝土抗氯离子渗
透能力比普通混凝土差．文献 [1—2]通过 ASTM
C1202法测定发现，再生混凝土氯离子扩散系数随
着再生细骨料掺量的增加而增大．Ann等L3 采用
ASTM C1202法研究了粉煤灰和粒化高炉矿渣对
再生混凝土抗氯离子渗透性的影响，结果表明，掺粉
煤灰和粒化高炉矿渣能够有效提高再生混凝土抗氯
离子渗透能力．陈爱玖等 ]通过 NEL法测定发现，
经过冻融循环后再生混凝土的氯离子扩散系数明显
增大．张健等采用 RCM 氯离子扩散系数试验方
法研究了水灰比、再生粗细骨料取代量和矿物掺合
料对再生混凝土氯离子渗透性的影响，结果显示，高
品质再生细骨料混凝土抗氯离子渗透性能优于天然
骨料混凝土，高品质再生粗骨料混凝土的抗氯离子
渗透性能接近天然粗骨料混凝土，掺超细矿粉或硅
灰可提高再生混凝土抗氯离子渗透能力．雷霆等 [6]
通过 ACMT法测定发现，采用掺合料裹骨料工艺可
大幅度提高再生混凝土抗氯离子渗透性能，对其后
期抗氯离子渗透性能也有提高，但幅度较小．在实际
工程中，扩散作用和毛细孑L吸附作用是氯离子迁移