再生混凝土物理力学性能试验研究

资料大小：260KB
资料类型：.PDF
资料等级：
发布时间：2021-10-29

资料介绍

采用废砖粗骨料、废混凝土细骨料完全替代天然骨料，配制了 5 组不同配合比的再生混凝土试块。通过
试验得到立方体试块的抗压强度、碳化深度以及棱柱体试块的轴心抗压强度、弹性模量、收缩等力学性能指标。经
分析得出轴心抗压强度与立方体抗压强度、弹性模量与抗压强度的关系，并对混凝土碳化和收缩公式进行了拟合。［关键词］再生混凝土; 抗压强度; 碳化; 收缩; 弹性模量
中图分类号: TU528 文献标识码: A 文章编号: 1002-848X( 2013) 01-0073-03 Experimental study on mechanical performances of recycled concrete Hao Tong，Shi Lei，Chen Jingjing ( School of Civil Engineering，Zhengzhou University，Zhengzhou 450002，China) Abstract: Preparation of five different mix of recycled brick concrete blocks was done． The compressive strength， carbonation depth，elastic modulus，shrinkage and other mechanical performances were obtained through the tests． The relationships between the axial compressive strength and cube compressive strength，elastic modulus and compressive strength were obtained． Carbonation and shrinkage formulas of concrete were also fitted． Keywords: recycled concrete; compressive strength; carbonation; shrinkage; elastic modulus * 2010 年度河南省墙改基金项目( 2010-18) 。
作者简介: 郝彤，博士，教授，Email: haotong@ zzu． edu． cn。 0 前言
再生混凝土是将废弃混凝土经过破碎、清洗、分级，然后按一定比例相互混合得到的“再生骨料”作
为粗骨料或粗、细骨料，加入水泥浆配制而成的混凝
土。本文用废砖粗骨料 100% 替代天然碎石、用废
混凝土细骨料 100% 替代天然砂制作混凝土，配制
了 5 组不同配合比的再生混凝土试块，进行试验得
到 3，7，28d 的立方体试块的抗压强度、碳化深度以
及棱柱体试块的轴心抗压强度、弹性模量、收缩等力
学性能指标，为再生混凝土墙板的研究奠定基础。 1 试验材料及试验方案
1. 1 试验材料
水泥: 河南某公司生产的复合硅酸盐水泥
PC32. 5; 水: 普通自来水; 骨料: 本文采用的骨料是
采用机械破碎后经人工筛分得到的废砖再生粗骨料
和废混凝土再生细骨料，骨料的基本物理性能如表
1 所示。
骨料的基本物理性能表 1
指标废砖再生粗骨料废混凝土再生细骨料
粒径范围 /mm 5 ～ 75 0 ～ 5
表观密度 / kg /m3 1 610 2 590
堆积密度 / kg /m3 775 1 198
紧密密度 / kg /m3 875 1 317
松散孔隙率 /% 52 54
紧密孔隙率 /% 46 49 24h 吸水率 /% 16. 3 5. 8
含水率 /% 0. 5 4. 7
细度模数 — 4. 7 1. 2 试验方案及配合比设计
与天然粗骨料相比较，废砖再生粗骨料的显著
特征之一是高吸水率，因此，再生混凝土单位用水量
是再生混凝土配合比设计中的关键，大部分学者提
出了基于自由水灰比的再生混凝土配合比设计方
法［1-5］，本试验也采用该方法配制 5 组不同配合比的
混凝土，依次命名为 RA，RB，RC，RD，RE，各组配合
比见表 2。