再生骨料级配对再生混凝土多孔砖干燥收缩的影响

资料大小：280KB
资料类型：.PDF
资料等级：
发布时间：2021-10-29

资料介绍

：对不同碎砖和细骨料含量的再生混凝土多孔砖进行干燥收缩率试验研究。结果表明，再生混凝土多孔砖干燥收缩率随碎
砖骨料掺量的增加而增大，随着细骨料掺量的增加而减小。
关键词：再生混凝土；多孔砖；配合比；骨料级配；干燥收缩
中图分类号：TU522．1 文献标识码：A 文章编号：1001—702X(2011)04—0024—04
Effect of aggregate gradation on drying shrinkage of recycled concrete perforated brick
HU Li，LIANG Jianguo，YANG We~un，LI Pen~ei
(School of Civil Engineering＆ Architecture，Changsha University of Science＆ Technology，Changsha 4101 14，Hunan，China)
Abstract：The drying shrinkage of recycled concrete perforated brick with different content of broken bricks and recycled fine
aggregate was tested．The test results show that the drying shrinkage of recycled concrete perforated brick increases with the rais—
ing of broken bricks content，and decreases with the raising of recycled fine aggregate content．
Key words：recycled concrete：perforated brick；mixture ratio：aggregate gradation：drying shrinkage
0 引言
随着城镇化建设步伐的加快，我国每年因城市改造拆除
的废旧建筑将产生大量的建筑垃圾，依照传统的方式占地堆
积处理，不仅浪费耕地，而且污染环境。据报道，长沙市 2003
年房屋拆迁面积 42．9万 m ，按每平方米产生 1．0 1．5 t建筑
垃圾计算，加上新建房屋产生的建筑垃圾，总量超过 100万
t，处理的费用更是高达 124．35元h。如何解决建筑垃圾的回
收和利用，对我国城镇化建设有着重要的意义。
将建筑垃圾经过专业生产工艺处理后得到的再生骨料具
有强度低、吸水率大、材料性能变异大等特点，再生混凝土强
度低、离散性大、和易性差、干燥收缩大等特点。目前国内对再
生混凝土多孔砖的干缩性能研究的较少，郑州大学刘立新等l】]
对再生碎混凝土集料多孔砖和碎砖集料多孔砖进行了干缩性
能研究，测得的收缩值分别为0．17 mm／m、0．10 mm／m。但该试
验研究中5 Him以下的采用天然砂，废弃的细小颗粒易造成
环境的二次污染。本研究通过改进多孔砖的生产工艺，增大砖
的成型压力，提高砖的密实度，从而提高砖的强度和耐久性，
收稿日期：2010—12—15
作者简介：胡利，男，1986年生，湖南岳阳人，硕士研究生。地址：长沙理
工大学云塘校区土木与建筑学院 887信箱，E-mail：514703801@qq．corn。
· 24· 新型建筑材料 2011．4
使得 5 mm以下的再生骨料得以全部利用。
本研究将对7种不同配合比的再生混凝土多孔砖进行干
燥收缩试验，重点研究再生骨料级配对再生混凝土多孔砖干
燥收缩性能的影响。
1 再生混凝土多孔砖用骨料性能及
配合比设计
再生骨料采用长沙市区废旧建筑拆下来的混凝土块和砖
块，经砖厂细碎机破碎和人工筛分工艺后得到粒径0—5 mm
的细骨料和粒径5 10 mm的粗骨料。按照标准试验方法[2-31，
得到再生骨料的基本物理性能指标见表 I。