养护剂对高性能混凝土渗透性的影响研究

资料大小：200KB
资料类型：.PDF
资料等级：
发布时间：2021-10-26

资料介绍

文章研究了养护荆对高性能混凝土在干燥条件下渗透性的影响。结果表明养护剂可以降低 28d碳化深度 25．O％
一 47．3％，降低混凝土表层吸水系数 31_3％一89．0％，降低混凝土电通量 1．2％一30．0％。养护剂 (特别是保水率较高养护剂)对混
凝土表层渗透性的降低作用更为显著。
[关键词】高性能混凝土；养护；养护剂；渗透性
【中 It1~ ]TU528．042 【文献标识码】A 【文章编号】l005—6270(2013)05—0092—02
Research on Effects of Curing Com pounds on Permeability of High Performance Concrete
KONG Xiang--fu LIHuo——xing
(Jiangsu Bote New Materials Co．，Ltd，Nanjing Jiangsu 210008 China)
Abstract：Effects of curing compounds on permeability of high performance concrete(HPC)under drying were
studied in this paper．The results indicated that 28d carbonation depth，surface water sorptivity coefficient and
electric flux could be reduced by 25．0％ -47．3％，31．3％ -89．0％ and 1．2％ -30．0％，respectively．Furtherm ore，
curing compounds especially for those with better capacity to reduce moisture loss could reduce perm eability of
surface concrete dramatically．
Key words：hi曲 performance concrete(HPC)；curing；curing compounds；permeablility
0 前言
养护是混凝土实现其设计性能的最重要因素之一．现
代高性能混凝土的特点使养护相比之前更为重要【l】：当今水
泥强度发展速度更快，允许拆模的试件更短．这在一定程度
上导致了工程中养护过早地结束：现代混凝土的水胶比较
低 (特别是对于高性能混凝土而言 )，白干燥现象更为显著．
外部的湿养也很难缓解此现象：现代混凝土工程多掺加矿
物掺合料，如粉煤灰、磨细矿渣，而矿物掺合料的水化速率
较慢．需要更长时间的养护以促进掺合料的水化。
我国幅员辽阔．以西北地区为代表的干旱及半干旱地
区，日照时间长，多风沙，且存在水资源匮乏和水资源利用成
本较高的问题。养护剂是一种喷洒或涂刷于混凝土表面．能
够形成一层连续不透水的密闭养护膜的乳液或高分子溶液．
将其作为混凝土保水养护材料．不仅可以解决养护所需水资
源匮乏的问题．同时也可以对传统养护方法不易养护的部位
(如结构的立面和坡面等)进行养护。可以较好的提高混凝土
的抗裂性和耐久性鲫。目前混凝土养护剂已在包括兰新铁路
在内的工程中获得成功应用。本文选取了 JC 901-2002(水
泥混凝土养护》规定的两种等级养护剂，研究了养护剂对对
高性能混凝土在干燥条件下渗透性的影响。
1 试验
1．1 原材料及配合比
原材料：小野田水泥有限公司生产 P·I1 52．5硅酸盐水
泥；南京热电厂 I级粉煤灰；江南 $95级磨细矿粉；Elken
微硅灰粉：细度模数为 2．6的河沙；5 mm 20 mm 连续级配
玄武岩碎石。混凝土配合比如表 1所示．通过调节混凝土减
水剂用量将初始坍落度控制在 18 cm一20 em。养护剂采用
江苏博特新材料有限公司生产的 Ereducer~201和 Ere．
ducer@301型养护剂．上述 2种养护剂分别满足 JC 901—
2002(水泥混凝土养护》中合格品和一等品要求。
1．2 养护条件
养护条件分为干养和养护剂养护 2种．养护龄期均为
表 l 混凝土配合比 (k