纤维素纤维及纤维混杂混凝土抗裂抗渗牲能的试验研究及工程应用

资料大小：300KB
资料类型：.PDF
资料等级：
发布时间：2021-10-24

资料介绍

研究了纤维素纤维、PVA纤维及其两者混杂掺入对混凝土抗裂抗渗性能的影响。结果表明，纤维素纤维和 PVA纤维均能
有效提高混凝土的抗裂抗渗性能，两者混杂掺入对混凝土抗裂抗渗性能的改善效果明显。依托工程应用表明，用于地下工程墙板中
纤维素纤维混凝土具有良好的抗裂抗渗性能和体积稳定性。
关键词：纤维；混杂；混凝土；抗裂抗渗；工程应用
中图分类号：TU528．572 文献标识码：B 文章编号：1001—702X(2012)03—0040—03
Experim ental study and engineering application of anti-cracking and impermeability pe rform ance of
concrete mixed with ceHulose fiber an d hybrid fiber
QIAN Hongping
(School of Civil Engineering，Changzhou Institute of Technology，Changzhou 213002，Jiangsu，China)
Abstract：In this paper，effects of the cellulose fiber，PVA fiber and hybrid fiber on concrete crack resistance and imperme—
abil．1y performance were studied．The test results show that，cellulose fiber and PVA fiber can improve the crack resistance and
impermeability of concrete，and the effect of hybrid fiber is obvious．Engineering application shows that，for underground engineering
wall of cellulose fiber concrete has good crack resistance’imperm eability and volume stability performance·
Key words：fiber；hybrid；concrete；crack resistance an d imperm eability；engineering application
随着我国城市基础设施建设规模的不断扩大，混凝土结
构耐久性和服役寿命的提高己成为工程界日益关注的问题，
良好的抗裂抗渗性能是确保混凝土具有较高耐久性的前提条
件。在混凝土中掺入纤维能明显改善和提高混凝土的抗拉强
度、极限延伸率、韧性及冲击性能等性能，对于钢纤维、聚丙烯
纤维等纤维的研究及实际工程应用已较为广泛【，而纤维素
纤维及其混杂纤维对混凝土抗裂抗渗；I生能影响的应用研究较
少。本文在混凝土中掺入纤维素纤维、PVA纤维及二者混杂
纤维，并在基体中掺加聚羧酸高效减水剂、粉煤灰和矿粉以改
善混凝土的综合性能。通过对纤维素纤维及其混杂纤维混凝
土的劈裂抗拉强度、早期塑性开裂、氯离子渗透系数等物理力
学性能的测试，对比分析纤维素纤维及其与PVA纤维混杂对
基金项目：江苏省交通厅科技计划项目(09Y18)
收稿日期：2011-09—15
作者简介：钱红萍，女，1966年生，江苏丹阳人，硕士，副教授，主要从
事土木工程材料的教学与研究。地址：常州市通江南路 299号，E—mail：
qianhp@czu．cn。
·40· 新型建筑材料 2012．3
混凝土抗裂抗渗性能的影响，为依托工程提供了抗裂抗渗性
能符合要求的混凝土配合比。 +
1 试验 ●
1．1 原材料
水泥，江苏嘉新水泥集团产京阳42．5级普通硅酸盐水泥，
其碱含量(Na20+0．658Kz0)为0．48％，各项性能符合GB l75—
2007《通用硅酸盐水泥》标准要求；粉煤灰，常州电厂的I级粉
煤灰；矿粉，常州中盛磨细矿粉公司提供；粗、细骨料，技术指
标符合JGJ 52--2006《普通混凝土用砂、石质量及检验方法》
标准要求；减水剂，江苏建科院有限公司生产的聚羧酸高效减
水剂；纤维，美国进口纤维素纤维和常州天怡纤维厂提供的
PVA纤维，2种纤维的物理力学性能见表