屋面保温用快硬泡沫混凝土性能研究

资料大小：250KB
资料类型：.PDF
资料等级：
发布时间：2021-10-23

资料介绍

：以硫铝酸盐水泥、泡沫剂和减水剂为主要原料，采用物理发泡法制备了密度等级在 300～600 ks／m 的屋面保温用
泡沫混凝土，它能快速成型，自然养护。3d抗压强度可达 393 kPa，且可满足对其导热系数的要求。
关键词：泡沫混凝土；硫铝酸盐水泥；屋面保温；试验
文章编号：1007—497X(2014)一15—0037—04 中图分类号：TU231；TU55 1 文献标识码：A
Research on Performance of Rapid Hardening Foam ed Concrete
for Therm al Insulation Roofing
Qiao Xinyuan ，Jiao Liye
(1．Dalian Harbor Bay Engineering Co．，Ltd．，Dalian，Liaoning 1 16020；
2．The 65585 Troop of Chinese People S Liberation Army，D~ian，Liaoning 1 16104)
Abstract：Sulphoaluminate cement，foaming agent and water reducer acted as main raw materials，foamed concrete for
thermal insulation roofing was fabricated with physical foaming method，its density grade is between 300 and 600 kg／cm3．
This concrete is rapid prototyping and natural curing，its 3d compressive strength can be up to 393kpa，and its properties also
satisfy the requirement for heat conductivity coeffi cient．
Key words：foamed concrete；sulphoaluminate cement；thermal insulation roofing；experiment
随着能源环境问题的日益得到重视，“绿色建筑”
的理念逐渐深人人心。屋面保温材料作为节能环保型
建筑的重要组成部分，其研究具有重大现实意义。目
前，我国常用的屋面保温材料主要有岩棉、膨胀珍珠
岩、膨胀蛭石、聚苯乙烯、聚氨酯以及泡沫混凝土等。
相比于前面几种材料或防水性能差、或防火隐患高的
缺陷，泡沫混凝土不仅耐水性能良好，且是 A级防火
材料『】I。国标 GB 50207--2012(屋面工程质量验收规
收稿日期：2014—06—26
基金项目：国家自然科学基金项目(项目编号：51102035)。
作者简介：乔欣元，男，1977年生，工程师，主要从事港口工程
建设管理及新型建筑材料研发。联系地址：116110大连市沙河
口区香西路 199—10号李茹(转 )。
范》中新增了“现浇泡沫混凝土保温层 ”的内容，也
是近年来泡沫混凝土在国内得到迅速推广并应用的
结果【5】。
泡沫混凝土作为屋面保温材料具有密度小、质量
轻、粘结力强、保温、防火、隔音、抗震等优点。在施工
中，泡沫混凝土还具有将保温层、找平层、找坡层合三
为一的特有优势，同时可兼作刚性防水层的辅助隔离
层，能够简化施工工序、缩短工期、节约成本，并能保
证工程质量 0l。泡沫混凝土在屋面上应用的构造示
意图，见图 1。
泡沫混凝土作为屋面保温材料，也存在露天施工
中受成型龄期制约、养护期受自然情况影响大【“】、强
度偏低等缺点。本文为克服上述缺点，采用硫铝酸盐