石灰消化性能及其对蒸压加气混凝土性能的影响

资料大小：200KB
资料类型：.PDF
资料等级：
发布时间：2021-10-18

资料介绍

研究石灰细度、有效CaO含量、初始温度、石膏种类和掺量对石灰消化性能的影响及石灰的消化性能对蒸压加气混凝土
性能的影响。结果表明，石灰的细度、初始温度以及石膏种类对石灰消化性能有明显影响；石灰中有效 CaO含量与其消化温度和消
化时间没有明显的相关性；石灰的消化性能显著影响加气混凝土料浆浇注稳定性和成品性能。在加气混凝土生产中，应控制适当的
石灰消化性能参数，以保证加气混凝土料浆发泡和稠化协调进行。
关键词：石灰；消化；加气混凝土；石膏；性能
中图分类号：TU522．3+2 文献标识码：A 文章编号：1001—702X(2011)09—0045—03
Slaking character of lim e and its effect Oil the performance of autoclaved aerated concrete
GU／Miaomiao，PENG 】unzhi，CAI Zhenzhe
(Xiamen Academy of Building Research Group Co．Ltd．，Xiamen 361004，Fujian，China)
Abstract：The effects of fineness，initial temperature，content of effective CaO and type and content of gypsum on the slaking
character of lime，as well as the effect of slaking character on the performance of autoclaved aerated concrete (AAC) were studied．
Results show that fineness，initial temperature and gypsum type had significant effect on the slaking character of lime，while content
of effective CaO had little correlation with the slaking temperature and slaking time．The slaking character of lime was a key factor to affect the casting stability and product performance of AAC，slaking parameters should be controlled in production process to
ensure the foaming and hardening of AAC slurry goes coordinatively．
Key words：lime；slaking character；aerated concrete：gypsum；perform ance
石灰是蒸压加气混凝土生产中的主要原材料之一，其主
要作用是：提供Ca0，并在水热条件下与硅质、铝质材料发生
反应，生成水化硅酸钙和水化铝酸钙，从而使制品获得强度；
提高加气混凝土料浆的碱度，满足铝粉发气条件；在加气混凝
土料浆发气稠化和坯体硬化阶段，提供足够的热源，促进坯体
的硬化。石灰的消化性能是评价石灰使用性能的主要指标，它
直接影响到加气混凝土生产配比和工艺，因此，对石灰消化性
能进行研究是指导和控制加气混凝土生产质量的前提。
国内对蒸压加气混凝土的性能及使用过程的质量问题已
有较多研究，但对于蒸压加气混凝土配比与工艺方面，特别是
石灰消化性能及其对加气混凝土的生产和性能的影响研究较
少¨】-3]。本文结合常青树建材(福建)有限公司的生产实践，研
究了石灰消化 I~iIII影响因素及其对蒸压加气混凝土性能的
收稿日期：2011-04—15
作者简介：桂苗苗，女，1975年生，山东蓬莱人，高级工程师，从事建
筑材料研发与管理。地址：福建省厦门市湖滨南路 62号，电话：0592—
2273796，E—mail：mututu@ 126．com。
影响。
l 实验
1．1 原材料
石灰：市售工业用生石灰，主要化学成分见表 1。石膏：市
售天然石膏和脱硫石膏，主要化学成分见表2。粉煤灰：嵩屿
电厂湿排灰。砂：漳州河砂，Si0 含量不低于75％。铝粉：市售
工业用铝粉膏。