桥梁混凝土破损锈蚀露筋修复涂层乳液的制备与研究

资料大小：350KB
资料类型：.PDF
资料等级：
发布时间：2021-10-15

资料介绍

选择合适的原料和合成工艺，采用高性能可聚合乳化剂，31入磷酸酯功能单体(EM一39)，以衣康酸单丁酯和
甲基丙烯酸缩水甘油酯为交联单体，通过活性有机硅氧烷对丙烯酸乳液进行改性，并合成水性丙烯酸防锈乳液。以
此乳液为基础，选择防锈剂，制备了水性丙烯酸防锈涂料，其可用于桥梁钢筋混凝土结构破损锈蚀露筋的修复。
关键词：改性丙烯酸防锈乳液；水性丙烯酸防锈涂料；混凝土破损露筋；修复研究
文章编号：1009—6477(2014)o4—0101—05 中图分类号：U449．7 文献标识码：A
Preparation and Study of Coating Emulsion for Repair of Damage，
Rusting and Exposed Reinforcing Bars of Concrete in Bridges
SHANG W u ，YU Zhaoyang ，ZHENG Xiaobin ，TU W eiping
Abstract：W ith monobutyl itaconate and glycidyl methacrylate as linking monomers，this paper modifies
acrylic emulsion via active organo—siloxane and synthesizes water-based acrylic anti—m st emulsion by
selecting appropriate raw materials and synthetic processes， adopting high—performance polymerizable
emulsifier and introducing functional phosphate monomers(EM-39)．With this emulsion as basis，the
paper selects antirust agents to prepare waster-based acrylic anti-rust coating，which can be used to repair
damage，rusting and exposed reinforcing bars of concrete structures in bridges．
Key words：modified acrylic anti—rust emulsion；water—based acrylic anti—ru st coating；damage and
exposed reinforcing bars of concrete；repair study
钢筋混凝土结构长期暴露在复杂的大气环境
中，由于昆凝土本身存在不致密、抗裂性差等缺点，
故环境中的腐蚀介质极易渗透到混凝土内部，致使
内部钢筋的锈蚀，并顺筋产生裂缝，从而影响混凝土
结构的稳定性和耐久性，降低桥梁的使用寿命 ¨ J。
对锈蚀露筋进行修复，首先需对破损露筋进行
防锈处理，阻止外部腐蚀性介质与钢筋接触。丙烯
酸乳液不仅具有优越的耐候性、耐老化性、耐腐蚀性
和粘接性，而且对环境污染小，价格相对低廉。本文
介绍采用有机硅对水性丙烯酸防锈乳液进行改性，
并用其制备水性防锈涂料。该涂料可对桥梁}昆凝土
破损锈蚀露筋进行修复。
1 试验
1．1 主要原料
制备桥梁混凝土破损锈蚀露筋修复涂层乳液的
基金项目：广东省交通运输厅科技项目(2013～02～05)
收稿日期：2014—04—02
作者简介：商武(1988一)，男，湖jE省麻城市人，在读研究生
主要原材料如下：甲基丙烯酸甲酯 (MMA)、丙烯酸
丁酯 (BA)、苯乙烯(st)、衣康酸单丁酯 (MBI)、甲基
丙烯酸缩水甘油酯 (GMA)、甲基丙烯酰氧基丙基三
甲氧基硅烷(KH一57O)、乙烯基三乙氧基硅烷 (YDH
一 151)、乙烯基三异丙氧基硅烷 (AC一76)，其均为分
析纯，由天津科密欧化学试剂有限公司生产；磷酸酯
(EM一39)，由长兴化学材料有限公司生产；DNS一
458、SR一10，其为化学纯，由广东双键贸易有限公司
生产；过硫酸钠、碳酸氢钠、三乙胺，其均为化学纯，
由上海凌风化学试剂有限公司生产；去离子水，自
制。
1．2 合成工艺
乳液预乳化工艺：将适量去离子水、复合乳化
剂、引发剂 (过硫酸钠 ) 昆合后搅拌至溶解，搅拌的
同时慢慢滴加混合单体 St、BA、GMA，待预乳化 15
min制得核预乳液备用。采用同样的方法制备壳乳