泡沫混凝土干燥收缩性能改性研究

资料大小：220KB
资料类型：.PDF
资料等级：
发布时间：2021-10-10

资料介绍

要：研究了泡沫混凝土在填充轻质骨料、复合有机聚合物后的干燥收缩特性。结果表明，泡沫混凝土干燥收缩主要来源于
毛细孔失水产生的收缩应力，填充体积稳定轻质骨料或复合憎水聚合物均有利于改善泡沫混凝土的干燥收缩性能。
关键词：泡沫混凝土；干燥收缩；骨料；毛细孔；憎水；改性
中图分类号：TU55 1_3 文献标识码：A 文章编号：1001—702X(2013)04—0072—03
M odification research Oil the dry shrinkage perform ance of foam concrete
ZHANG Guoyong，CHEN Yongpan，ZENG Xianchun，WANG Li
(Zhejiang Academy of Building Research＆ Design Co．Ltd．，Hangzhou 310012，Zh~iang，China)
Abstract：The dry shrinkage performances of foam concrete filled with lightweight aggregate and organic polymer are
studied．The results shOW that the dry shrinkage of foam concrete is primarily from shrinkage stress due to evaporation of micro
pore water．Filled with volume stabile lightweight aggregate or hydrophobic organic polymer will significantly improve the drying
shrinkage perform ance of foam concrete．
Key words：foam concrete；dry shrinkage；aggregate；micro pores；hydrophobic：modification
0 引言
物理发泡泡沫混凝土是用物理方法将泡沫剂水溶液制
成泡沫，再将泡沫加入到由水泥、掺合料、外加剂和水等制成
的料浆中，经混合搅拌、浇注成型、养护制成【 -3]o由于泡沫混
凝土含有大量封闭孔隙，具有轻质、保温、隔热等物理性能，
同时保留水泥基材料的防火、耐久等优点，适用于夏热冬冷
地区建筑外墙保温材料Iq，受到人们广泛的关注。然而，泡沫
混凝土因缺少骨料且一般采用自然养护，其干燥收缩(干缩)
值较大，可达普通混凝土的6 10倍[5-0]，阻碍了其在建筑保温
领域的推广应用。本文主要研究泡沫混凝土的干缩机理，并
通过改性试验研究降低泡沫混凝土的干缩率。
l 试验
1．1 原材料
水泥：P·042．5水泥；发泡剂：HTQ一1型复合发泡剂，河南
华泰建材开发有限公司；减水剂：35％浓度聚羧酸盐高效减水
收稿日期：2012—10—31
作者简介：张国永，男，1984年生，福建莆田人，硕士。地址：杭州市文
二路 28号，电话：0571—88277301。
·72· 新型建筑材料 2013．4
剂；纤维：混凝土工程用聚丙烯纤维；空心玻璃微珠：BLO14型
微珠，秦皇岛秦皇玻璃微珠有限公司；乳胶粉：80W可再分散
乳胶粉，国民淀粉产；憎水剂：SEAL80憎水剂，易莱泰产。
1．2 主要设备
搅拌机：符合GB／T 17671--1999(~g泥胶砂强度检验方法
(ISO法)》的要求；发泡器：河南华泰建材开发有限公司，H10
型。
1-3 试验方法
1．3．1 泡沫混凝土的制备
调节发泡器参数，将一定浓度的泡沫剂水溶液制成均匀、
细小、稳定的泡沫。按设定比例计量水泥、纤维等干物料，用搅
拌机搅拌均匀后加入水和减水剂拌成浆料，再向浆料中加入
一定体积的泡沫，继续搅拌至均匀。将泡沫混凝土拌合物浇制
成型，成型好的试件在自然通风室内静置2 d后脱模，移至标
准养护条件环境中养护至龄期。
泡沫混凝土配合比设计通过控制干物料的总质量和泡沫
混凝土浆料的总体积进行，并在配制时检测泡沫混凝土的湿
密度，进而控制泡沫混凝土的干密度。
1．3．2 干缩值测试方法
泡沫混凝土试件干缩值测试参照lJGJ 70—2OO9《建筑砂
浆基本性能试验方法》进行，不同之处在于，干缩测试前根