在混凝土中掺入纳米 SiO 制备高性能混凝土,测试其力学性能。结果表明,对于同一种的混凝土,掺不同量的纳米 SiOz
后均 能不 同程度地提高混凝土的抗压强度 ,其 中当纳米 SiO 掺量为 3%时,7 d龄期 的混凝土抗压强度增强效果 明显 ,较基 准混 凝土
提 高 8.4%。
关键 词:纳米SiO ;高性能混凝土;水胶比;抗压强度
中图分类号 :TU528.59 文献标识码 :B 文章编号 :1001—702X(2012)07—0078-03
Influence of nano SiO2 on mechanical property of the high performance concrete
ZHANG Haiyan, Yon~un
(Construction Engineering,Sanmenxia Polytechnic,Sanmenxia 472000,Henan,China)
Abstract:In this paper,the high performance concrete is prepared by adding nano Si02 into concrete,and its mechanical
properties are tested.The result shows that for the same kind of concrete,the early and late concrete compressive strength is im—
proved in different degrees by adding different amount of nano SiO:·and when the percentage of nano Si02 is 3% ,the compressive
strength of concrete in 7 days is improved observably,which is 8-4% up compared to the reference concrete.
K ey words:nano SiO2;high performance concrete;water-binder ratio;compressive strength
高性能混凝土是以耐久性为主要目标进行设计的,具有
早期强度高、捌 好、体积稳定性高、在严酷环境下使用寿命
较长等优点_l-2]。因而很多国家都对高性能混凝土进行了大量
的研究开发,并广泛应用在土木工程中。
纳米材料是指颗粒尺寸在纳米尺度范围内(1—100 nm)的
超细材料,是处在原子簇和宏观物体交界的过渡区域 。纳米
材料在混凝土中的应用研究始于20世纪90年代。目前的主
要研究领域包括纳米 Si0 对混凝土物理和化学性能的改变
及其机理、纳米 Si0 与硅灰等纳米混合材料对混凝土的力
学、物化以及耐久性等性能的影响 。但是在实际工程应用
领域,纳米 SiO 对高性能混凝土力学性能影响的研究还不是
很完善。因此,本文制备的高性能混凝土就是在特定混凝土中
基金项 目:科技部科技人员服务企业资助项 目(2009GJD0o016):
河南省教育厅 自然科学基金项 目(201 1A460o05)
收稿 日期:2012—04—13
作者简介:张海燕 ,女,1975年生 ,河南三 门峡人,硕士,讲师 。E—mail
zhxypp-1@ 163.con。
·78· 新 型建 筑材 料 2012.7
掺不同量纳米SiO ,并对试样进行力学性能测试,分析不同纳
米SiO 掺量的高性能混凝土的抗压强度变化趋势,从而为高
性能混凝土在实际工程应用方面提供理论支持。
1 试 验
1.1 试 验材料
水泥:崤山牌42.5级普通硅酸盐水泥。
粗集料:选用三门峡市观音堂石场生产的石灰质碎石,其
中粒径为10 25 mm的碎石占30%,粒径为25—40 mm的碎
石占70%。
细集料:选用三门峡市涧河沙场的河砂,细度模数2.7,粒
径 5 10mm。
因为上述粗、细集料使用前均经自来水冲洗并烘干,所以
可以忽略其含泥量与含水率。
粉煤灰选用长治市易天粉煤灰有限公司生产的Ⅱ级粉煤
灰;硅灰选用洛阳济禾微硅粉有限公司生产的微硅粉。
外加剂:选用上海 巴斯夫化学公司生产的DH-4005聚羧
酸盐减水剂、河南洛阳科尔公司生产的 DH一2型水泥增强剂