采用煤矸石为主要原料 ,制备 了一种新型的泡沫混凝土。在煤矸石泡沫混凝土强度试验的基础上 ,通过正交试验的方
法 ,研究了不同水泥与煤矸石比例、水料比、减水剂 占胶凝材料比例等因素对掺泡沫前料浆流动度的影响,取最佳用量的一组 ,分
别设计低 、中、高三个表观密度等级 ,进行掺泡试验 ,结果发现这种混凝土在泡沫量很大的前提下仍然有 比较理想 的使用强度 ,可
以用来生产不 同需求的混凝土制品。
关键词 : 煤矸石 ;泡沫混凝土 ;流动度 ;强度
中图分类号 : TU528.2 文献标志码: A 文章编号 : 1002—3550(2013)06—0132—04
Research on preparation of coal gangue foam concrete
CH D彻 , 匠N u瑚 ,LIUKaiping,LIUNine,BAO Junmin
(School ofMaterials Science and Engineering ofChangan University,Xi’an 710061,China)
Abstract: A new type of f0aIl1 concrete product was prepared by use of coal gan gue as the main raw materia1.Concrete strength was
based on a series ofexperiments.Meanwhile,themainfactors affecting slurryfluidity were studiedincluding ratio ofcement/coal gangue,
thedosagewater andwater reducerbythemethodoforthogonal experiment.Thebest groupwas chosenan dan ddesignlow ,medium ,an d
high density grade.then put into use offoam experiment.It was discovered that this concrete still had a relatively ideal intensity ofuse and
three density grade met the properties requirements ofstrength and density ofthe foamed concrete products.
Key words: coal gangue;foam concrete;fluidity;strength
O 引 言
煤矸石是我国排放量最大的工业 固体废弃物 ,煤矸石
的长期堆放 ,不仅 占用 大量 土地 ,也带来 了一系列的环境
问题。中国作为以煤为主要能源的国家 ,加大煤矸石的综合
利用迫在眉睫。另一方 面,作为 目前普遍使用的有机建筑保
温材 料 ,其 老化性 、安全性能等一系列问题在很大程度地
限制 了建筑保温材料的广泛应用。本课题 以煤矸石 为主要
原料研制了一种新型的建筑用无机保温材料 ,具有较好 的
化学稳定性和耐水性 ,克服 了传统有机保温材料 的缺点 。
1 试 验 部 分
1.1 原材料及技术性能
本研究所用水泥由陕西尧柏特种水泥有限公司提供,
为 P·O 42.5R级水泥 ,细度为 4%(筛析 法 ),初 凝时 间为
180 min,终凝 时间为 249 min,其化学 成分见表 1,在泡 沫
混凝 土中起 到胶凝作用 ,提供 主要强度来源 。
表 1 水泥的化学成分 %
SiO2 Fe203 AI203 CaO MgO SO3 总碱量 Loss
22.02 2.65 6.】9 58.99 2.53 2.67 0 70 3 08
本试验所选取 的煤矸石来 自陕西铜川地 区,经煅烧 、粉
磨及过筛后使用 。煤矸石 的 XRD射线衍射采用 Et本理学
D/max2400X射线衍射仪进行 。试 验条件 :40 kV,100 mA,
Cu靶 ,扫描范围为 5~~70。,扫描速度为 10。/min。分析 图见
图 1。从图中可 以看出煅烧后的煤矸石主要成分是石英 、高
岭石 、赤铁矿和石灰石以及部分非晶相物质。