e electromagnetic induction method is the most commonly used method for the thick—
ness detection of concrete cover．However，the testing result is affected by many factors．In order to im—
prove detection precision of the detection，the 25-metre T beam in the bridge standard drawing published
by the Ministry of Communications is studied．Through the indoor experiment，the influence of the space
of the distributed reinforcement was analyzed based on the measurement result．W ith calculation and anal—
ysis，the calibration formula was fitted to modify the thickness detection of the concrete cover．Through
the field test，it has been verified that it can improve precision of the detection．The research results con—
tribute to the test and construction control over the thickness detection of concrete cover．
[Key words]bridge engineering；calibration method；thickness detection of concrete cover；exper．
iment；computational formula；testing precision
1 概 述
在 混凝 土 结构 工程 设 计 中 ，钢 筋 保护 层 厚度 是
一 个 重要 指标 。钢筋保 护层厚 度 的确定 是根据 2个
因素 ：① 在结 构 上 能保 证 钢 筋 与 混 凝 土共 同作 用 ，
即满足 受力钢 筋的粘 结锚 固要求 ；② 应 保证 混 凝 土
中钢筋 的耐久 性 … 。如果 保 护 层厚 度不 足 ，钢 筋 发
生锈蚀 后 ，在 钢 筋 表 面 出 现 锈 斑 ，钢筋 与混 凝 土 脱
开 ，引 起钢筋 与混凝 土 的粘结力 下 降 ，导致 构件 承载
力下 降 ；混凝 土保 护层厚 度不 足 ，外 界有 害介质 容易
穿透 保护层 的裂缝 到达 钢 筋 表 面 ，造 成 钢 筋锈 蚀 膨
胀 ，混凝 土 开裂 ，甚 至崩 裂脱 落 ，进 而加 速 钢 筋 锈 蚀
破坏 。沿海 地 区因混凝 土保 护层厚 度不 足引 起 的钢
筋混凝 土结 构破坏 速度 比内陆地 区快 得多 。混凝 土
保护层 越厚 ，对结 构耐久 性越 有利 ，但 在结构 截 面尺
寸不 变的条 件下 ，会使构 件有 效截 面 尺寸减小 ，承载
力降低 。因此在 施工 过 程 中 要 加强 质 量 控 制 ，提
高保护 层 厚度测 试 精 度 ，保 证 混 凝 土 保 护层 满 足规
范要 求 ，避 免造 成重 大安全 事故 。
电磁 感应 法检 测钢筋 保护 层厚 度是 最常用 的方
法 。采用 电 磁感应 原 理 进行 钢筋 检 测 ，即利 用 信 号
发 射装 置产 生一定 频 率 的 交 变 电磁 场 ，激 发 混 凝 土

因本站资料资源较多，启用了多个文件服务器，如果浏览器下载较慢，请调用迅雷下载，特别是超过了5M以上的文件！请一定调用迅雷，有时候速度就会飞起哦，如果您的浏览器自动加载了PDF预览，文件太大又卡死，请按下载说明里的把PDF插件关闭了就可以直接下载，不会再预览了！