路用透水型彩色再生混凝土的耐久性能研究

资料大小：230KB
资料类型：.PDF
资料等级：
发布时间：2021-10-08

资料介绍

研究了掺加建筑垃圾的混凝土骨料制备的路用透水型彩色再生混凝土的抗冻融性能、抗碳化性能和耐
磨性能与水胶比、聚丙烯纤维掺量、及颜料掺量的关系。结果表明，水胶比对路用透水型彩色再生混凝土的冻融性
能、碳化性能和耐磨性能均有明显的影响；掺加矿渣对路用透水型彩色再生混凝土的冻融性能有较明显的有利的影
响．对碳化性能和耐磨性有不利的影响。适量添加聚丙烯纤维对混凝土耐磨性能和冻融性能有一定有利影响，但掺
加太多有不利影响．掺聚丙烯使透水性能显著降低，对碳化性能无明显影响。颜料掺量对彩色再生透水混凝土的透
水性能、冻融性能、碳化性能和耐磨性能等耐久性能方面无明显的影响。
关键词：透水再生混凝土；冻融性能；碳化性能；耐磨性能
Abstract：The permeable color recycled road concrete for medium traffic road is prepared by adding the construction
waste，and the relationship of between the durability property of the concrete and some preparation condition is studied by
the orthogonat test．The result shows that the water—binder ratio has an obvious effect on freezing—thawing．carbonation
and wear——resisting of the concrete；adding the slag can enhance freezing——thawing and wear——resisting properties of the
concrete，but isn’t good for the carbonation and wear-resisting properties of the concrete；adding polypropylene fiber has a
favorable effect on freezing-thawing and wear -resisting properties of the concrete in a certain content，but has no obvious
effect on carbonation．In addition，pigment content almost has no effect on the durability property of concrete．
Key words：Permeable recycled concrete；Freezing—thawing；Carbonation；W ear-resisting
中图分类号：TU528 文献标识码：A 文章编号：1000—4637(2014)02—83—04
0 前言
路用透水型彩色再生混凝土是一种低碳环保
型混凝土．具有透水性和透气性。可以使雨水回流
至地面下．透气性可以调节地面空气的温度，减少
“热导效应 ”的危害[1]。同时，透水路面雨水及时回
流。减少了下雨路面反光的现象，可减少安全事故。
透水混凝土骨料中掺加再生混凝土骨料圆，可减少
建筑垃圾，变废为宝。透水混凝土可通过调整配合
比、水胶比等参数使强度达到路面混凝土的透水性
能和强度要求。路用透水型彩色再生混凝土已有应
用实例，但路用透水型彩色再生混凝土耐久性能方
面研究的比较少。本文通过正交试验[3]，在保证透水
系数和抗压强度满足要求的前提下，通过改变水胶
比和掺人纤维、改变颜料掺量及矿渣掺量，研究了
透水混凝土的冻融性能、耐磨性能及碳化性能等耐
久性能，可为实际施工提供依据。
1 试验概况
1．1 试验用原材料
水泥：P·O 42．5级普通硅酸盐水泥
粗骨料：天然骨料为本地碎石，再生骨料为试
验室废弃混凝土试块经破碎、筛分、高温烘烤加工
而成。粗骨料的基本物理性能见表 1。
矿渣：商品矿渣，化学成分见表 2。
聚丙烯纤维：TB一19束状单丝纤维。