对河砂混凝土和淡化海砂混凝土在 5%Na2SO (质量分数 ,下 同)、5%MGSO4+3.5%C1 腐蚀溶液 中浸泡和浸烘 的损伤过
究。结果表明:两种试验制度下,河砂混凝土的动弹模损失大于同配合 比的淡化海砂混凝土 ;浸烘试验中,淡化混凝土的动弹
低 40%,河砂混凝土约为 60%。
词 : 淡化海砂 ;硫酸盐腐蚀 ;动弹模
分类号 : TU528.01 文献标志码 : A 文章编号: 1002—3550(2013)01—0021—03
Research on corrosion to washed sea sand concrete attacked by sulfate
SUQing,CHENAi-rong
(DepartmentofBridgeEngineering,TongjiUniversity,Shanghai200092,China)
tract: Thedamageprocessofordinaryconcreteandwashed sea sandconcrete,attackedby solutionsof5%Na2SO4(inmass,samebe一
, 5%M GSO4+3.5%C1一with method ofimmersion an d drying—immersion were studied.The results showed that the loss ofelastic modu—
fordinary concrete w as much m ore than that ofwashed sea san d concrete.At th e end ofdrying—imm ersion experim ent,th e relative dyC elastic modulus ofwashed sea sand concrete was nearly 0.6,which ofordinary concerete was 0.4.The deterioration ofconcrete pre·
in elastic modulus was stable。then decreased.
w ords: washed sea sand;sulfate corrosion:dynamic elastic modulus
危砂是一种低附加值的非金属矿种 ,运 费在建筑砂
戈本中 占有较大的密度 ,“地理区位因素”决定 了建
平采和利用的模式是就地取材 、因地制宜 。多年来
设使 以宁波 、舟山为代表的沿海城市的海砂开采 、
丑形成了一定规模[i-z](图 1)。关于海砂混凝土性能
献 也 日渐丰富 ,但研究热点大多是“海砂型 ”氯盐
冈筋锈蚀 ,忽视了滨海环境 中硫酸盐也是引起混凝
对久性能劣化的重要原 因。
(a)采砂设备 (b)满载而归的运砂船和岸边的砂场
图 1 宁波一舟山地区颇具规模的海砂开采业
本研 究针对滨海环境 条件 ,以 5%Na2SO 、5%MGS04+
3.5%C1溶液为腐蚀介质 ,采用 了长期浸泡腐蚀和浸烘循环
两 种试 验制度对 比研究相 同配合 比的河砂与淡化海砂混
凝土 的损伤失效过程 。
1 试 验
1.1 原材料
山水水泥厂 P·O 42.5级水泥 ,物理性能见表 1。II级粉
煤 灰的化学成分见 表 2。聚羧 酸系高效减水剂 。粗 骨料为
5~25 mm的碎石 ,细骨料的性能指标见表 3。
表 1 P·O 42.5级水泥的物理力学性能
1.2 混 凝 土 配合 比
淡化海砂 混凝 土在我 国沿海地 区应用较 广 ,尤 以宁
波 、舟山为代表 。因此 ,本试验在参考上述地区混凝土配合
比的基础上 ,根据配合 比设计要求 ,进行大量试配得到表 4
所示的配合 比。试验试件为边长 100 mill的立方体。