矿物掺合料对C100混凝土早期收缩及干缩的影响

资料大小：260KB
资料类型：.PDF
资料等级：
发布时间：2021-09-28

资料介绍

矿物掺合料对 C1 OO混凝土早期收缩及
干缩的影响
徐仁崇，李晓斌，桂苗苗江达宣
(厦门市建筑科学研究院集团股份有限公司，361004)
，
摘要：研究了复掺情况下，矿物掺合料种类及掺量对 C100高强混凝土早期收缩及干燥收缩的影响。结果表
明，混凝土的早期收缩和干燥收缩随着粉煤灰掺量的增加逐渐减少，粉煤灰对早期收缩的抑制作用优于干燥收缩；
随着矿粉掺量的增加，混凝土的早期收缩增大而干燥收缩减少；硅灰的掺入增大了混凝土的早期收缩与干燥收缩，
且随着硅灰掺量的增加，这种作用更加明显。
关键词：矿物掺合料；C100混凝土；早期收缩；干燥收缩
Abstract：Effects of category and dosage of mineral admixtures on the early age and drying shrinkage of C100 high
strength concrete with mixing condition are investigated．The results indicate that the early age and drying shrinkage will
decrease with the increase dosage of fly ash，and the effect on reducing early age shrinkage is better than that of reducing
drying shrinkage．The early age shrinkage will increase and the drying shrinkage will decrease when the dosage of ground
granulated blast furnace slag inereases．Silica fume can increase the early age and drying shrinkage of concrete，and the
effect will be more obvious when the increasing dosage of silica fume．
Key words：Mineral admixtures；C 100 concrete；Early shrinkage；Drying shrinkage
中图分类号：TU528．31 文献标识码：A 文章编号：1000—4637(2013)01—24—04
0 前言
建筑物的高层化、大跨化及重载化发展使高强
混凝土的应用日益广泛，抗压强度为 C100的超高
强混凝土已经开始在实际工程中得以应用『】-2]。超高
强度混凝土具有优异的耐久性能，但是由于其水泥
用量大、水胶比低、水化热大，在实际推广应用过程
中遇到了很大阻力，超高强混凝土的早期开裂问题
已经引起了广泛关注。
掺加矿物掺合料是改善高强混凝土工作性能、
延缓水化放热、减少混凝土收缩裂缝的有效措施『3_。
国内外学者在矿物掺合料对混凝土收缩影响及其
作用机理方面做了大量的研究工作，主要集中在
水胶比大于 0．3的情况，但是对于水胶比低于 0．25
的超高强混凝土很少涉及。本文采用 0．23的水胶比
配制 C100混凝土，研究粉煤灰 (10％、20％和 30％)、
矿粉 (6％、12％和 18％)与硅灰 (0％、5％和 10％)在
复掺情况下对 C100高强混凝土早期收缩及干燥收
缩性能的影响，以期为 C100高强混凝土的工程应
用提供技术参考。
1 原材料与试验方法
基金项目：厦门市科技计划资助项目(3502Z20100044)。
— — 24 ——
1．1 原材料
水泥：福建产 42．5级普通硅酸盐水泥，其物理
性能指标见表 1；粉煤灰：漳州产的 Ⅱ级粉煤灰，细
度 14．6％，需水量比 97％，烧失量 1．45％；矿粉：$95
级矿渣粉，比表面积 410m／／kg，流动度比 100％；硅
灰：厦门产，比表面积约为 18000m2／kg，SiO：含量
92．3％；碎石：反击破花岗岩碎石，粒径为 5~20mm；
河砂：厦门产的中砂，细度模数