矿物掺合料对C100～C120超高强混凝土基本性能的影响

资料大小：250KB
资料类型：.PDF
资料等级：
发布时间：2021-09-28

资料介绍

矿物掺合料对 C1 00~C1 20超高强混凝土
基本性能的影响
王斌，李晓欢，徐芬莲，苏华
(中建商品混凝土成都有限公司 610052)
摘要：通过正交试验考察了胶凝材料总量、水泥用量及超细粉煤灰用量对超高强混凝土抗压强度的影响，研
究了硅灰、超细粉煤灰与复合硅材等矿物掺合料对 C100~C120超高强混凝土基本性能的影响。结果表明，对超高强
混凝土强度影响最主要的因素是水泥在胶凝材料中所占的比例；超细粉煤灰与硅灰复掺对超高强混凝土工作性能
与强度改善效果较好；复合硅材对超高强混凝土的工作性能与强度均有一定的提高。
关键词：超高强混凝土；超细粉煤灰；硅灰；复合硅材；正交试验
Abstract：The influences of total amount cementitious material，cement content and ultra-fine fly ash dosage on the
compressive strength of ultra-hi【gh strength concrete are studied by orthogonal test．The effects of mineral admixtures such
as silica fume，ultra-fine fly ash and siliceous admixture on the basic properties of C100~C120 ultra．high strength con—
crete are researched．The results show that the main affected factor on the compress strength of ultra-high strength con—
crete is the proportion of cement in the cementitious materia1．Compounding both ultra—fine fly ash and silica fume is bet—
ter for the workability and strength of the ultra-high strength concrete．At the same time，siliceous admixture also has the
improvement on the workability and strength of the ultra—high strength concrete．
Key words：Ultra-high strength concrete；Ultra-fine fly ash；Silica fume；Siliceous admixture；Orthogonal test
中图分类号：TU528 文献标识码：A 文章编号：1000—4637(2012)03-10-04
0 前言
2O世纪混凝土科学与工程技术取得了重大成
就，高性能混凝土的应用极大地推动了混凝土科技
的进步，促进了人类社会的发展 [1】。随着 2l世纪混
凝土工程的大型化、工程环境的复杂化以及应用领
域的不断扩大，人们对其提出了更高的要求，混凝
土材料的高强化和高性能化是 2l世纪混凝土科学
和工程技术发展的重要方向闭。
矿物掺合料已经成为商品混凝土中不可缺少
的一个组分，随着研究工作的不断深入，以及实际
工程应用经验的积累，对矿物掺合料的认识也发生
了很大的变化。随着高强高性能混凝土的研究与应
用，发现一些工业废渣与天然矿物具有许多优良的
特性，它可以改善混凝土的许多性质。这些矿物掺
合料不再作为一种 “废弃物 ”而加以利用，而是作为
一种宝贵的资源用于改善混凝土的性能【3J。
矿物掺合料品种繁多’，其组成和性能也各有不
同，在实际使用时应根据工程实际情况合理选择，
充分发挥和利用矿物掺合料的优良特性，尽可能避
免或减弱其所带来的不良影响，本文分析了超细粉
煤灰、硅灰与复合硅材等矿物掺合料对超高强混凝
土的工作性能及抗压强度的影响。
1 原材料
(1)水泥：四川某水泥厂生产的 P·042．5级水
泥，其物理力学性能检测结果见