混凝土渗透结晶材料在水工
喷射混凝土中的应用
刘 玲 ，王可良 ，郑灿堂
(1．济南德利泰建材科技有限公司，250010；2．山东水利科学研究院，济南250014)
摘要：为研究渗透结晶材料对喷射混凝土性能的影响，采用抗渗和抗冻试验方法，结合扫描电子显微(SEM)
和压汞(MIP)对混凝土的微观结构进行分析和表征。结果表明，渗透结晶材料可提高喷射混凝土的抗渗和抗冻性
能，通过改善混凝土界面过渡区和水泥石的微观结构，改善混凝土的孔径分布，使少害孔含量增多，多害孔含量减
少，最可几孔径减小，混凝土贯通能力减弱，抗渗和抗冻性能提高。
关键词：混凝土；渗透结晶材料；抗渗性；抗冻性；微观结构
Abstract：In order to study the influences of permeated crystalline materials on perform ances of shoclete，combining
with MIP and SEM，the mierostructule of concrete is analyzed and characterized by imperm eability and fieezing—thaw
cycle test methods． nle results show that perm eated crystalline materials can improve the perform an ces of imperm eability
and freezing—thaw cycle of shotcrete．It is because that perm eated crystalline materials can impmve the micmstmctule of
interfacial transition zone of concrete an d cement stone，improve the pore size distribution of concrete，which make mole
content of less harmful pores and less content of harmful pores．Therefore，most probab le pore size of concrete reduces and
the perform ances of imperm eability and freezing-thaw cycle of concrete are improved．
Key words：Concrete；Perm eated crystalline materials；Imperm eability；Freezing-thaw cycle；Microstructule
中图分类号：TU528 文献标识码：A 文章编号：1o0O-4637(2011)12—15—04
0 前言
喷射混凝土是借助喷射机械将混凝土高速喷
射到受喷面上凝结硬化而成的混凝土，其一般采用
较小的水灰比，与石、混凝土及钢材等有很高的粘
结强度。喷射混凝土不受场地和其他条件限制，工
序简单，可与其他工种平行作业，工期短，施工速度
快，工程质量可靠，是一种先进的施工方 ”。由于
喷射混凝土具有以上特点，目前已被广泛应用于交
通隧道、边坡、深基坑支护、水工隧洞的施工，也常
应用于各种结构物的修复和大坝的除险加固等[2-3]。
喷射混凝土由于其特殊的施工工艺和配合比，混凝
土在硬化过程中，更容易出现不同程度的裂缝，导
致混凝土的抗渗和抗冻融性能急剧下降。混凝土渗
透结晶材料中含有的活性化学物质通过载体向混
凝土内部渗透，并在混凝上中形成不溶于水的结晶
体，填塞混凝土中的毛细孔道及宏观微裂缝，从而
使混凝土致密、防水M ，提高喷射混凝土的耐久性。
1 试验
1．1 试验原材料与配合比
水泥：P·042．5级水泥，青州产；细骨料：中砂，细
度模数2．6，青州产；粗骨料：5mm碎石，青州产；引
气减水剂：液体，青州产；速凝剂：粉体，青州产；渗
透结晶材料：自制。按SL352—2006(水工混凝土试验
规程》和GB50086—2001《锚杆喷射混凝土支护技