混凝土抗渗试验封模方法改进研究

资料大小：250KB
资料类型：.PDF
资料等级：
发布时间：2021-09-18

资料介绍

混凝土抗渗试验封模方法改进研究
杨萍马良袁晓宁杨进超陈曼
(西北核技术研究所，西安710024)
[摘要] 针对混凝土抗渗试验中密封效果差的问题，对抗渗试验密封材料的封模方法进行了探讨，指出了利用冷封
模方法来代替热封模方法进行抗渗试验是一种可行、经济、环保、方便的方法。通过大量试验表明，混凝土
抗渗试验采用腻子作密封材料涂抹于试件上并采取辅助措施封模效果最好，在水压高达2．5 MPa时试件未
出现边缘透水现象。
[关键词] 混凝土；抗渗；封模方法
[中图分类号】TU502 ．4 [文献标志码] A [文章编号] 1001—523X(2010)11-0017-03
[Abstract]
[Keywords]
M ETHoDS oF SEALD G M oULD IN CoNCRETE
ANTI．PERM EABILITY TESTS
Yang Ping Ma Liang Yuan Xiao—-ning Yang Jin--chao Chen min
Various methods of sealing mould were investigated to solve the problem of poor sealing effect in concrete anti—
permeability tests．The results indicate that the cold type of sealing mould，which uses putty as sealing material tO
coat the concrete samples with some other complementary measures，is feasible to substitute for the hot type of
sealing mould．The phenomena of water leakage between the mould and the concrete test block didn’t come up until
the hydraulic pressure of automatic pressurized concrete permeability meter was up to 2．5 MPa．
concrete；anti—perm eability；sealing mould
在我国建筑工程行业中，国标《普通混凝土长期性能和
耐久性能试验方法》(GBJ 82—1985)和建设部标准《普通混
凝土配合比设计规程》(JGJ 55—2O00)都规定了采用渗水法
检测混凝土的抗渗性能，即给受检混凝土逐级增加水压，使
水在混凝土中迁移，通过检验混凝土承受的最大水压或水在
混凝土中的渗透深度，来描述混凝土的抗渗性能。这种试验
方法成败的关键环节是将涂抹密封材料的混凝土试件装入
试模后(简称“封模”)能否保证压力水不从试件与试模接触
处渗出。因此，采用适宜的密封材料达成的封模效果，对试
验成败来说，显得尤为重要。但是，1986年7月1日施行
的国标GBJ 82—1985已经执行了将近20年，未曾更新过一
次，在具体的试验中发现许多弊端，密封材料需要加热熔化，
试模也需要用烘箱预热(简称“热封模方法”)，操作方法繁
重复杂，混凝土抗渗试验经常由于密封材料的封模效果不佳
而引起对混凝土抗渗等级的判定受到影响。本文以渗水法
手段检测混凝土抗渗性能为基础进行研究，以不同的密封材
料作对比试验，探索出不需要加热的封模方法(简称“冷封模
收稿日期：2010—08—15
作者简介：杨萍(1972-)，女，N Jll绵阳人，毕业于装备指挥技术学院
本科学历，工程师，主要从事工程材料检验及研究工作。
方法)，期望给混凝土抗渗试验提供一些可行的参考。
I 热封模方法抗渗试验
1．I 试验方法
试验过程参照国标GBJ 82— 1985进行：6个混凝土试件
养护至试验前一天从标准养护室内取出，将表面晾干并擦拭
干净，然后把掺有石蜡和松香的密封材料按质量比为1：4的
比例加热熔化，待完全熔化后将密封材料均匀滚涂在试件内
侧壁上，随即用压力机将试件压人试模中，加压至试件与试
模底面平齐，待试模冷却后方可解除压力，