混凝土假性碳化引起回弹法检测强度的误判
王海潮， 吕莉
(北京陆建鸿兴工程质量检测有限公司，北京 100040)
[摘 要] 混凝土碳化能提高其表面硬度，现行混凝土强度检测规程把碳化深度作为回弹法检测混凝土强度的
一个修正系数来采用。研究发现在某种特定的状态下测定的碳化值不—定是实质意义上的混凝土碳
化深度。研究揭示了回弹法检测中酚酞试剂指示假性碳化引起混凝土检测强度评判的误区。
[关键词] 无损检测；碳化；回弹法
[中图分类号] Tu 5828 [文献标志码]B [文章编号] 1001—523X(2015)12—0035—02
CoNCRETE STRENGTH M ISJUDGM ENT CAUSED BY SPURIoUS
CARBoNIZATIoN IN REBoUND M ETHoD
WangHai—chao，Lyu“
[Abstract] Carbonation could improve the surface hardness of concrete．Current specification for concrete strength
determination by rebound method used the carbonation depth as a compensation factor in concrete
strength determination by rebound method．It was found that the carbonization detected under a specific
state may not be the real carbonization depth of concrete．This paper pointed out the concrete s~ength
determ ination mistake caused by spur ious carbonization indicated by phenolphthalein indicator in the
rebound method．
[Keywords] nondestructive detection；carbonization；rebound method
硅酸盐水泥主要由石灰质原料和粘土质原
料组成，石灰质原料提供CaO，CaO是碱性物质。
新拌混凝土由于水化作用形成Ca(OH) 。水泥
浆在空气中硬化时表面水化形成的Ca(OH)：会
收稿日期：2015—1 10
作者简介：王海潮(198O一)，男，北京市人，工程师，e—mail
haichao2728@sina．com。
与空气中的CO，反应生成CaCO ，此反应称
为混凝土的碳化。混凝土的碳化速度及碳化深
度不仅与混凝土水灰比及自身的密实度有关，
还与混凝土所处的环境条件有关，如空气中的
CO，浓度和空气的相对湿度等。
由于碳化的收缩，CaCO 的生成能提高混
凝土的表面强度，且碳化深度与混凝土龄期接