混凝土保护层质量与钢筋锈蚀

资料大小：200KB
资料类型：.PDF
资料等级：
发布时间：2021-09-17

资料介绍

混凝土保护层质量与钢筋锈蚀
林乐琴
(乐清市水利局，浙江乐清325600)
摘要：防止钢筋锈蚀是提高水工钢筋混凝土结构耐久性一个重要因素．从结构设计角度探讨了混凝土碳化和钢
筋锈蚀产生机理，并根据实测数据分析了钢筋锈蚀与保护层厚度之间的关系，认为钢筋的锈蚀在很大程度上取决
于混凝土保护层的质量，并进而认为保护层密实性和必需厚度是保护混凝土保护层质量控制的关键．
关键词：钢筋；混凝土；保护层
中图分类号：TU375 文献标志码：A 文章编号：1008—536X(2013)02—0017—03
On Concrete Protective Layer Quality and Reinforcement Corrosion
LIN Yue—qin
(Yueqing Water Conservancy Bureau，Yueqing 325600，China)
Abstract：Corrosion protection of reinforcing bar is an important way to improve the lasting of concrete structure．The reason
of concrete carbonation and reinforcing bar corrosion are discussed in this paper in the view of structure design．According
to the measured data，the relationship between reinforcing bar corrosion and the quality of concrete protection layer is also
analyzed in the paper．W ith analyzing the influencing factor of the concrete protection layer quality，it proves that the density
and necessary thickness of concrete protection layer is very important to quality contro1．
Key words：reinforcing bar；concrete；protective layer
0 引言
根据近年来国内外实际调查资料可知，水工钢
筋混凝土结构中，因钢筋的锈蚀而引起构件损坏，
甚至整个结构失效的事例屡见不鲜，问题的严重性
已越来越引起人们的重视¨ ．
混凝土中钢筋锈蚀有两种情况：一种是先裂后
锈，另一种是先锈后裂．一般构件表面无裂缝，由于
腐蚀气体介质从保护层中全面涌透，扩散到钢筋表
面而导致钢筋的锈蚀，引起钢筋体积膨胀(钢筋锈
蚀产物—— 铁锈的体积比原来大2～4倍)使混凝
土保护层产生相当大的拉力，造成混凝土保护层顺
着钢筋方向开裂，削落而破坏．这种先锈后裂类型
与横向裂缝关系不大，主要与保护层有关．当然，钢
筋的锈蚀还与结构所处的环境、构件受力方式等因
素有关．
对于混凝土材料的耐久性问题长期以来已经
收稿日期：2013—04-20
作者简介：林乐琴(1978一)，女，浙江乐清人，工程师．从事水利
工程质量监督．
得到了广泛深入研究．但是混凝土的耐久性不应当
仅在材料问题上进行分析和评价，而应当把混凝土
材料放在构件和工程结构的整体中进行研究和评
价．外界环境对混凝土材料的腐蚀与损伤主要发生
在混凝土的浅层，进而使得混凝土截面和强度受到
损失，影响结构的外观和安全．对于钢筋混凝土结
构，更重要的是因表层混凝土发生腐蚀或损伤而削
弱了对钢筋的保护能力，加速钢筋锈蚀进程．
混凝土保护层一般定义为钢筋外表面到混凝
土构件表面的这层混凝土，位于钢筋与外界环境之
间，是保护钢筋及内部混凝土不受外界侵蚀的重要
防线，对钢筋混凝土结构耐久性具有十分重要的意
义．因此，对于混凝土保护层的结构与性能需要进
行深入研究．
1 钢筋的锈蚀
钢筋在混凝土中锈蚀是一种特定的电化学腐
蚀．通常条件下，混凝土中孔隙水为水泥水化时析
出的大量氢氧化钙和少数钾、钠氢氧化物．PH值约
为12．5～l3．5之间．在这种高碱性环境中，钢筋表