硅灰高强混凝土超声测强及影响因素研究

资料大小：320KB
资料类型：.PDF
资料等级：
发布时间：2021-09-16

资料介绍

缪群李为杜
(上海市建筑科学研究院,上海 200032) (同济大学,上海200092)
摘要用超声波法对掺硅灰高强混凝土的力学性能进行了研究,结果表明,超声波声速与硅
灰高强混凝土强度之间存在着良好的相关性,同时得出了本试验条件下的回归方程式,并就养护制
度、龄期及含水率等因素对其超声测强的影响进行了分析。
主题词混凝土超声检验强度
STUDY ON ULTRASONIC STRENGTH TESTING OF THE HIGH-STRENGTH
CONCRETE WITH SILICA PLASTER AND ITS AFFECTING FACTORS
Miao Qun Li Weidu
(Shanghai Research Institute of Building Science)(Tongji University,Shanghai)
Abstract Mechanical properties of the high-strength concrete with silica plaster were studied by ultrasonic
technique. Results showed that sound velocity of ultrasonic waves had good relationship with the strength of high-
strength concrete.The regression equation under the experimental condition was obtained.Factors affecting ultra-
sonic strength testing were analyzed such as maintenance rules, duration and moisture content.
Keywords Concrete Ultrasonic testing Strength
1高强混凝土检测概况段控制高强混凝土结构质量将成为突出问题。现阶
段的高强混凝土质量检测方法仍以试件破损试验为
混凝土的高强化已成为混凝土工业发展的必然主,现行的无损检测规程及局部破损检测方法目前
趋势,特别是80年代以来,英、美、日、澳等国家对高也多数局限于C50以下的普通混凝土范围,高强混
强混凝土的开发应用已达到了一个新的高度,工程凝土现场无损检测手段尚属空白,因此,研究高强混
实例从高层建筑到桥梁、钻井平台不一而足,取得了凝土的无损检测技术对完善检测、评估体系和消除
很好的经济和技术效果。我国的应用实践虽起步较工程质量隐患具有现实意义。
晚,但随着建筑业与国际的日趋接轨,建筑形式开始超声法以其应用简便、实用性强的特点在现场
向大跨、超高层方向发展,以上海为例,“东方明混凝土的无损检测中占有重要地位[21。本研究利用
珠”电视塔高468m,为亚洲第一高塔;内环29.2km 超声法,对强度等级为C50~C80的掺硅灰高强混
的连续高架路创中国高架路长度之最;金茂大厦近凝土的强度性能及测强影响因素进行了研究,结果
400m高,为世界第三高层建筑。工程技术的高难度表明,超声法在硅灰高强混凝土测强中具有很好的
对材料提出了严格要求,最近建设部已将高强高性适用性。
能混凝土技术列为重点推广应用的十项新技术之 2 试验过程
一,高强混凝土的推广应用势在必行。
近几年来,随着工程建设的迅速发展,对高强混 2.1 原材料选用
凝土的技术路线、生产工艺和施工规范的研究工作 (1)水泥:采用525号普通硅酸盐水泥,细度
已全面展开,在一些地区的工程中已开始部分应用 4.8%,28d抗折强度为9.2MPa,抗压强度为64.2
高强混凝土。由于高强混凝土的质量全面控制和现 MPa。
场检测要求比普通混凝土高,如何利用无损检测手 (2)硅灰:贵州铁合金厂生产