格构式泡沫混凝土节能墙体受力性能分析

资料大小：350KB
资料类型：.PDF
资料等级：
发布时间：2021-09-15

资料介绍

格构式泡沫混凝土节能墙体受力性能分析
路淼，薛春霞
(江苏大学土木工程与力学学院，江苏镇江212013)
摘要：通过水平低周反复荷载试验，对两组格构式节能墙体的破坏过程及钢筋应变进行了研究。结果表明，格构
式节能墙体的破坏过程经历了弹性阶段、弹塑性阶段和破坏阶段。肋梁、肋柱与墙板能够很好的协同工作，外框柱
承担整体弯矩，肋梁承担水平剪力，肋柱分担部分水平荷载，墙板承担抗侧刚度。
关键词：格构式节能墙体；破坏过程；应变
中图分类号：TU311 文献标志码：A 文章编号：1008—1933(2013)06—060—06
M echanical performance analysis of lattice of foam
concrete energy saving wall
LU Miao．XUE Chunxia
(School of Civil Engineering&Mechanics，Jiangsu University，Zhenjiang 212013，China)
Abstract：Based on hofizontM cyclic loading test，the paper discussed the failure process and reinforced strain of lattice energy saving
wal1．The results show that the destruction of the lattice energy saving wall experienced the elastic stage，the elastic—plastic stage and
failure stage．Ribbed，fibbed column and wall panels call work well together，frame column assume the overall moment，fibbed assume
the horizontal shear，ribbed column assume the part of the hofizontM load，the wallboard assume lateral stifness．
Key words：lattice energy saving wall；failure process；strain
0 前言周反复荷载试验，以此来研究墙体的受力性能。
格构式节能墙体使用肋梁、肋柱及内嵌材料泡
沫混凝土形成整体墙板，墙板又与外框架整浇为一
体，形成一个完整的受力体系。在水平荷载作用下
格构式节能墙板与外框架共同工作，墙板一方面受
到框架的约束作用，另一方面又对框架进行反约束，
两者相互作用、共同受力、充分发挥各自性能¨ 。
本文通过对两组节能墙体P．1及PJ．1进行水平低
1 试验概况
试验的构件设计为带构造柱的框架墙体，墙体
尺寸为1／2缩尺模型，每组的墙体尺寸相同，试验分
为两组：P组是泡沫混凝土墙体，编号为P一1；PJ组
是配钢筋网架的泡沫混凝土墙体，编号为PJ一1。各
试件尺寸及配筋见表l。
表1 试件尺寸
Table 1 Sample size
试件外框架混凝土强度等级为C30，框架梁、柱
主筋等级为HRB335，肋梁、柱钢筋、箍筋等级为
HPB235；试件P一1和试件PJ．1的泡沫混凝土强度等
级均为A3(B07)级；试件PJ．1内铺有双层钢筋网
收稿日期：2012-05-28
作者简介：路淼(1956一)，男，江苏镇江人，教授，研究方向为工程
结构中的力学问题。
E—mail：srhs_ 810@ 126．com
片，钢筋直径4 mm，间距200 mm，钢筋等级为
HPB235。
加载装置采用水平低周反复加载制度，采用荷
载和位移混合控制的加载制度_2 J。试件在屈服前
采用荷载控制，试件屈服后采用位移控制。判断试
件屈服的标准是滞回曲线上出现明显的拐点。试件
屈服后，取此时的位移为屈服位移，接着转为位移控
制。在位移控制阶段，以屈服位移为级差，分级加