高性能再生骨料混凝土力学性能的研究
刘立，赵顺增，曹淑萍，吴勇，贾福杰
(中国建筑材料科学研究总院，北京100024)
摘要：研究了不同水胶比、不同再生骨料替代率的高性能再生混凝土抗压强度、抗折强度、劈裂抗拉强度、弹
性模量等力学性能。结果显示，再生混凝土的强度等级在C30~C60之间，抗折强度大于4MPa，劈裂抗拉强度大于
2MPa，弹性模量在20~40GPa之间，力学性能满足应用技术要求。再生骨料替代率在60％以内时，不影响混凝土各项
强度指标；100％再生骨料替代率的混凝土根据水胶比不同，抗压强度降低5％~25％；再生混凝土弹性模量随再生骨
料替代率的增加而逐步降低。
关键词：再生混凝土；抗压强度；抗折强度；劈裂抗拉强度；弹性模量
Abstract： rhe mechanical properties such as compressive strength flexural strength，splitting tensile strength and e—
lastic modulus of high-performance recycled aggregate concrete with different water-binder ratio and recycled aggregate
replacement rate are studied．The results show that the strength of concrete is between C30一C60．flexural strength is more
than 4MPa，splitting tensile strength is more than 2MPa and elastic modulus is between 20-40GPa，the mechanical properties
can meet the application requirements．When the recycled aggregate replacement rate is less than 60％，there are no
influences on the strength indexes of recycled concrete，while the concrete with 100％ recycled aggregate replacement rate
can reduce the compressive strength of 5％-25％ according to the water-binder ratio，and the elastic modulus of recycled
aggregate concrete reduces with the increase of recycled aggregate replacement rate．
Key words：Recycled concrete；Compressive strength；Flexural strength；Splitting tensile strength；Elastic modulus
中图分类号：TU528 文献标识码：A 文章编号：10o0—4637(201 1)06—01—04
0 前言
随着社会经济的高速发展，建筑垃圾日益成为
人们关注的热点问题Ⅲ。目前，我国每年拆除建筑产
生的固体废弃物达2亿t以上，新建建筑产生的固
体废弃物约1亿t，两项合计约3亿t以上，这些没
有再利用的建筑垃圾对环境构成了严重的威胁，违
背了我国可持续发展的战略圆。
本文利用工业化生产的再生粗骨料，采用普通
硅酸盐水泥、粉煤灰、磨细矿渣粉等复合胶凝材料
及聚羧酸高效减水剂，设计了不同强度等级、不同
再生粗骨料取代率的高性能再生混凝土，系统研究
了再生混凝土的抗压强度、抗折强度、劈裂抗拉强
度以及弹性模量等力学指标的发展规律及其影响
因素。
1 试验原材料及混凝土配合比
1．1 试验原材料
水泥：42．5级普硅水泥。
基金项目：国家高技术研究发展计划“固体建筑废弃材料再
生混凝土资源化综合利用关键技术研究与应用”
(2009AA032301)。
粉煤灰：Ⅱ级粉煤灰。
磨细矿渣粉：$95级，比表面积400mZ／kg。
细骨料：中砂，细度模数2．5。
粗骨料：石灰岩碎石，最大粒径31．5mm。
减水剂：聚羧酸高效减水剂。
再生粗骨料：采用天津市某环保制品有限公司
生产的最大粒径31．5mm和10mm两种规格的废混
凝土再生粗骨料，性能见表1。