高拱坝混凝土真实抗压强度试验研究

资料大小：300KB
资料类型：.PDF
资料等级：
发布时间：2021-09-14

资料介绍

高拱坝混凝土真实抗压强度试验研究
肖延亮
(中国水电顾问集团成都勘测设计研究院，四川成都610072)
摘要：对高拱坝混凝土真实强度的试验研究表明，全级配混凝土与湿筛混凝土性能存在较大差异，减磨状态下混
凝土强度低于无减磨的混凝土．圆柱体试件的强度比立方体试件低。故高拱坝工程应进行系统的全级配混凝土试
验．为设计提供可靠的参数。
关键词：全级配混凝土；湿筛混凝土；性能真值；减磨；圆柱体试件；高拱坝
Study on the Real Compressive Strength of High—arch Dam Concrete
Xiao Yanliang
(Hydroehina Chengdu Engineering Corporation，Chengdu Sichuan 610072)
Abstract：The eompressive strength experiments show that the perfornmnees between the fullY——graded and wet——screened
concrete have great differences．the strength 0f grinding concrete is lower than the strength of not—grinding concrete，and the
strength of cylinder specimens is lower than the cube specimens．Therefore，fully—graded concrete experiment should be
carried out for high-arch dam and to provide reliable design parameters．
Key W ords：fully——graded concrete；wet——screened concrete；real properties；grinding；cylinders；high——arch dam
中图分类号：TV642．4：TV431 文献标识码：A 文章编号：0559—9342(2010)01—0103-03
0 引言
我国西部可开发的水能资源约2．743亿kW ．占
全同的72％．目前的开发率还不到15％．预计到
2020年开发率将达到60％7E右．未来十多年我国将
处于大规模水利水电T 程建设阶段⋯ 西部的水能资
源富集于崇山峻岭之问．很多位置适合建造混凝土
拱坝相对于重力坝而言．采用拱坝可以减少混凝
土量60％以上．大大降低工程费用 20世纪初我国
已建成了坝高240 lX1的二滩拱坝．标志着我同的拱
坝设计、施T 技术已达到国际先进水平随着科学
技术的不断进步．大坝的高度快速增加，目前在建
的小湾和锦屏一级大坝坝高达到300 m 级．且断面
厚高比愈来愈小混凝土重力坝的应力不高，用湿
筛混凝土进行试验并采用经验安全系数法可以满足
坝体设计和安全运行要求．．对于高拱坝．结构设计
必须采用先进的试验方法．进行仿真试验研究，为
设计提供真实可靠的试验数据．保证所建大坝既安
全可靠又经济耐久
1 粗骨料级配对混凝土抗压强度的影响
受试验条件的限制，通常采用湿筛二级配混凝
土小试件的方法来评定全级配混凝土的有关特性。
但湿筛混凝土剔除了粒径40 mm 以上的粗骨料。单
位体积粗骨料的含量由70％左右减少为30％左右．
而混凝土单位体积的胶材用量大大增加．使混凝土
的力学特性及相应的本构关系发生了较大变化。因
此．用湿筛混凝土小试件的试验结果来评价全级配
混凝土的有关特性．只是一种预先约定的相对评价
标准．而不能较为真实地反映拱坝全级配混凝土的
力学特性】冈此．有必要开展高拱坝全级配混凝土
仿真试验．丁解高拱坝混凝土的真实性能。
溪洛渡拱坝和锦屏一级拱坝全级配与湿筛混凝
土抗压强度对比试验结果见表1 全级配混凝土采
用边长为45 c113的立方体大试件．而湿筛混凝土采
用边为15 cm 的立方体小试件
从表1可知：
f 1)伞级配混凝土7 d抗压强度高于同水胶比
的湿筛混凝土．其原因可能有两个：一是湿筛混凝
土小试件采用振动台(2 850次／min)成型。而全级