钢筋与再生混凝土握裹力的试验研究

资料大小：300KB
资料类型：.PDF
资料等级：
发布时间：2021-09-13

资料介绍

钢筋与再生混凝土握裹力的试验研究
杨海涛，田石柱，
(1．哈尔滨工业大学土木工程学院，150090；2．苏州科技学院土木工程学院，215011)
摘要：以废弃混凝土为原料配制再生混凝土。通过对再生混凝土进行拉拔试验，研究再生粗骨料取代率和水灰
比对再生混凝土的握裹力及抗压强度的影响，并对试验现象进行了分析和总结。结果表明，再生混凝土的粘结强度大
于普通混凝土的粘结强度，并对水灰比给出了合理的取值范围，为再生混凝土的进一步推广应用提供了试验依据。
关键词：再生混凝土；拉拔试验；再生粗骨料取代率；握裹力；抗压强度
Abstract：Recycled concrete is prepared by the waste concrete as aggregate materials．Through the pull—out test
related to recycled concrete，the effects of recycled coarse aggregate replacement rate and cement—water ratio on the bond
stress and compressive strength of recycled concrete are studied．From the experiment and the analysis，the cohesional
strength of recycled concrete is stronger than that of common concrete．Rational range of cement—water ratio is given and
it can provide theoretical basis for further application Of recycled concrete．
Key words：Recycled concrete；Pull-out test；Recycled coarse aggregate replacement rate；Bond stress；Compressive
strength
中图分类号：TU528．571 文献标识码：A 文章编号：1000-4637(2013)03-06-05
0 前言
近年来，伴随着我国国民经济持续快速增长，
城市基础设施的升级和改造也得到了迅猛发展。一
方面，城市建设中一些老旧的建筑物、构造物被拆
除，由此产生了大量以废弃混凝土为主的建筑垃
圾，这些建筑垃圾不仅占用土地，而且对环境也造
成了污染。另一方面，大量建筑项目的启动，对混凝
土的需求量也变得越来越大，这就需要开采大量的
天然砂、石来供应。将废弃混凝土进行回收利用，不
但解决了土地占用和环境污染问题，而且有利于自
然资源的保护。
将从老旧建筑物上拆除下来的废弃混凝土经
清洗、加工、破碎和分级后，按一定的比例相互配
合，作为部分或全部骨料配制而成的混凝土称为再
生混凝土『1]。在再生混凝土研究和利用方面，同国外
相比，我国起步较晚，但近几年随着研究的不断深
入，研究成果也越来越丰富，但多数的研究工作是
围绕着提高再生骨料混凝土的强度及改善其力学
性能展开的[2-5l，对再生混凝土与钢筋粘结性能的研
究还不多见。本文主要对再生混凝土与钢筋之间的
握裹力进行研究，考察不同再生粗骨料取代率和水
灰比条件下握裹强度的变化，为再生混凝土的推广
应用提供试验依据。
1 试验
1．1 原材料
水泥：选用P·0 42．5级普通硅酸盐水泥，具体
性能见表l、表2。
细骨料：天然中砂，级配合格，表观密度为