干湿循环下氯盐-硫酸盐共同作用时混凝土耐久性研究初探

资料大小：240KB
资料类型：.PDF
资料等级：
发布时间：2021-09-12

资料介绍

干湿循环下氯盐一硫酸盐共同作用时
混凝土耐久性研究初探
彭高鹏，杜雷，周茗如
(1．兰州理工大学土木212程学院，甘肃兰州730050；2．甘肃土木工程科学研究院，甘肃兰州730020)
摘要：为了探求在西部盐渍土环境下混凝土耐久性问题，本文基于胶砂试块和不同浓度的氯盐与硫酸盐混合溶
液，利用干湿循环加速制度对其进行合理组合，以此来探求混凝土的腐蚀前期的损伤机理。
关键字：混凝土；干湿循环；耐久性
中图分类号：TU528 文献标识码：B
The Preliminary Investigation on Concrete Durability in Dry-wet
Circulation Cycles under the Chloride and Sulfate Environment
PENG Gao．peng ，DU Lei ，ZHOU Ming ru
(1．Lanzhou University of Technology，Lanzhou 730050，China；2．Gansu Civil Engineering Science Research Institute。lanzhou 730020，China)
Abstract：In order to explore the concrete durability under the conditions of salty soil in the west．based on cements—deter·
mination specimens and mixed solutions of sulfate and chloride with different concentration，reasonable combinations was
conducted by dry·wet cimulation to investigate the damage mechanism of concrete in early stage of coFro$ion．
Key W ords：concrete；drying—immersion cycles；durability
1 引言
我国西部地区盐渍土(一种土层内合有石膏、
芒硝、岩盐(硫酸盐或氯化物)等易溶盐且其含量大
于0．5％的土)分布广泛，新疆、青海、西藏、甘肃、宁
夏以及内蒙古等地均有大面积的盐渍区⋯ ，气候条
件以干旱少雨为主、早晚温差大、夏季炎热、冬季寒
冷、紫外线辐射较沿海地区高、不少地区土壤的碱、
盐含量高。一些重要设施如民航机场、高等级公路、
铁路桥梁、大型渡槽以及重要工业与民用建筑都直
接建立在盐渍土及严寒地区、甚至盐湖地区 J，以
盐渍土的化学腐蚀为主的耐久性破坏较为常见，然
而，当前关于混凝土在氯盐一硫酸盐共同作用下的
损伤研究成果并不多见，对于氯盐、硫酸盐在混凝土
损伤过程中的交互作用研究尚没有统一而明确的认
识。本文针对我国西部地区严酷工作环境，以及国
内外耐久性研究现状，在实验研究方面，考虑我国西
部地区盐渍土中的氯离子、硫酸根等腐蚀离子，以及
干燥的气候条件，对混凝土耐久性研究以双重腐蚀
环境，以及考虑干湿循环等因素，进行合理的组合，
使实验室实验尽量模拟西部盐渍土及干燥条件下混
凝土面临的损伤因素，从而探求多重破坏因素作用
下混凝土耐久性损伤机理。
2 实验原材料及实验方案
2．1 原材料
水泥：兰州五泉山水泥有限责任公司生产的
P．O 52．5水泥，水泥熟料的化学组成如表1，水泥的
物理力学性能如表1、表2所示。
砂为ISO标准砂，各级预配合以1 350±5 g量
的塑料袋混合包装，水为自来水，温度20±2℃ 。