粉煤灰对混凝土耐磨性能的影响
Effects of Fly Ash on W ear Resistant Ability of Concrete
赵晓妍，王文杰
(湖南212大联智桥隧技术有限公司，湖南长沙410011)
摘要：研究了粉煤灰掺量对混凝土不同龄期耐磨性能的影响，结果表明：混凝土早期耐磨性能随粉煤灰掺量增加而降低，但
混凝土后期耐磨性能随粉煤灰掺量增加而提高， 当粉煤灰掺量为30％ 时，混凝土的后期耐磨性能最佳，粉煤灰因活性
较低，掺入会降低混凝土早期耐磨性能；粉煤灰颗粒的高耐磨性和在后期粉煤灰火山灰效应的发挥是提高混凝土后期耐
磨性能的主要原因。
关键词：粉煤灰；混凝土；耐磨性能
中图分类号：TU528．2 文献标识码：A
Abstraet： he effects of the amount of fly ash on wear resistant ability of concrete at different ages were studied．The results
showed that：the wear resistant ability of concrete reduced as the amount of fly ash increased at early age．but the wear resistant
ability of concrete increased as the amount Of fly ash increased at 1ater age：when the amount of fly ash was 3O％ ．the wear
resistant ability of concrete at later age was the best；due to low activity of fly ash，the mix of fly ash would reduce wear resistant
ability of concrete at early age；the high wear resistant ability of fly ash particles and the pozzolanic action of fly ash at later age
were the main reasons improving the wear resistant ability of concrete at later age．
Key word：fly ash；concrete：wear resistant ability
0前言
随着现代交通量增加，超载和重载现象日益严重，混
凝土路面因磨损破坏引发的问题逐渐引起了国内外研究机
构与人员的注意，并展开了相关的研究工作。路面混凝土
的耐磨性能很大程度上取决于其表面性能，而混凝土的表
面性能主要受其原材料组成、抹面方式和养护条件等因素
的影响，因此，这些因素也是影响混凝土耐磨性能的主要
因素。
迄今为止，国内外很多研究人员已对混凝土的耐磨性
能进行了研究 。 。本文主要研究粉煤灰对混凝土耐磨性能
的影响规律，为混凝土(耐磨性能满足要求)配合比设计
提供理论上的依据。
1原材料及试验方案
1．1原材料
水泥(C)：长沙坪塘水泥有限公司生产的太平牌
P042．5水泥，化学成分及主要性能指标见表1和表2。
粉煤灰(FA)：湘潭电厂生产的I级粉煤灰，密度为
2．62 g／cm ，比表面积为460 m ／kg，需水量比为96％，化
学成分见表1。
16 COA三ASH 5／2010
表1 水泥和粉煤灰的化学成分
NN／％ 凝结时间／m-n
80 m筛筛余初凝 终凝
靛性标准稠度 竺 ：
用水量／％ 3 d 28 d
天然集料(NG)：碎石，级配合格，符合5—31．5mm
的连续级配要求。
砂fs)：湘江河砂，级配合格，细度模数2．61，符合
Ⅱ 区要求。
水fw1：自来水。
1．2试验方案
试验过程中，为了消除其他因素的影响，采用单因素
试验方法，研究粉煤灰对混凝土耐磨性的影响规律。
试件在试验室制作，采用60 L强制式搅拌机搅拌，
振动台振动成型，标准条件下养护至试验龄期后进行试验。
立方体抗压强度所用试件尺寸为100 mm×100 mm×100
mm；耐磨性能按照JTGE3 0-2005《公路工程水泥及水泥