废弃玻璃细骨料混凝土试验研究

资料大小：200KB
资料类型：.PDF
资料等级：
发布时间：2021-09-11

资料介绍

废弃玻璃细骨料混凝土试验研究
梁炯丰一，李爱飞，杨凤
(1．东华理工大学建筑工程学院，南昌330013；2．西安建筑科技大学土木工程学院，710055)
摘要：研究了废弃玻璃细骨料取代率对废弃玻璃细骨料混凝土拌和物坍落度和硬化废弃玻璃细骨料混凝土
立方体抗压强度、轴心抗压强度、劈裂抗拉强度、弹性模量的影响规律。试验结果表明，随着废弃玻璃细骨料取代率
的增大，其立方体抗压强度、轴心抗压强度、劈裂抗拉强度、弹性模量总体呈降低趋势；废弃玻璃细骨料混凝土的立
方体抗压强度、轴心抗压强度和劈裂抗拉强度与普通混凝土的破坏形式及变化规律相类似。
关键词：废弃玻璃细骨料；混凝土；强度
Abstract：The influences of waste glass fine aggregate replacement ratio on the mixture slump，the cubic and axial
compressive strength，the splitting-tensile strength and elastic modulus of the waste glass fine aggregate concrete are re_
searched．The experimental results show that with the increase of the waste glass fine aggreg~e replace ratio，the cubic
and axial compressive strength．the splitting-tensile strength and elastic modulus are reduced．rI1he destruction and the
change rule of the cubic and axial compressive strength and the splitting—tensile strength are similar between waste glass
fine aggregate concrete and ordinary concrete．
Key words：Waste glass fine aggregate；Concrete；Strength
中图分类号：TU528 文献标识码：A 文章编号：1000—4637I2013)07—80-03
0 前言
随着经济的发展。城市的废弃玻璃日益增多，
这些废弃玻璃部分被重新加工成新玻璃，大部分被
作为废物填埋掉。因此，将废弃玻璃作为混凝土骨
料再生利用正在成为人们关注的热点【。废弃玻璃
混凝土的研制，不仅开辟了废玻璃回收利用的新途
径。而且节约了有限的砂石资源，有益于国家节能
减排目标的实现。因此，笔者对废弃玻璃作为细骨
料的混凝土基本性能进行了试验研究，以期为废弃
玻璃资源化利用提供参考。
1 试验概况。
试验用原材料有42．5R级普通硅酸盐水泥，28d
抗压强度51．2MPa；天然细骨料为河砂，细度模数
2．6；天然粗骨料为连续级配的碎石，最大粒径25
mE；碎玻璃来自废品回收站收购的废弃玻璃，经人
工破碎为细骨料，其物理特性见表l。
表1 废弃玻璃细骨料的物理性能指标
基金项目：中国博士后科学基金项目(20080440814)；江西省
青年科学基金项目(20122BAB216005)；江西省教育厅青年
科学基金项目(GJJ12393)。
一80一
参考JGJ 55-2000(普通混凝土配合比设计规
程》的配合比设计方法，按等体积废玻璃替代砂子，
并将废玻璃质量计人砂率公式的设计方法进行设
计。所有试件采用0．43的同一水灰比，细骨料取代
率从0、20％、40％、60％、80％到100％变化，废弃玻
璃细骨料混凝土配合比见表2。
表2 废弃玻璃细骨料混凝土配合比 kg／m
废弃玻璃细骨料混凝土拌合物均采用容量为
50L的搅拌机进行机械搅拌，试件经振捣成型后，在
标准条件下养护3d、7d、14d和28d后取出进行相
关试验。立方体抗压强度和劈裂抗拉强度试验采用
边长150ram的标准立方体试件，轴心抗压强度和弹
性模量试验分别采用150mmxl50mmx450mm 和
150mmx150mmx300mm 的标准棱柱体试件．试验方
法按照GB／T 50o81—20O2《普通混凝土力学性能试
验方法标准》进行阁。