大掺量钢矿渣复合粉混凝土基本性能试验研究

资料大小：250KB
资料类型：.PDF
资料等级：
发布时间：2021-09-08

资料介绍

大掺量钢矿渣复合粉混凝土基本性能试验研究
李阳
(上海市建筑科学研究院，200032)
摘要：对普通混凝土、大掺量矿渣粉混凝土和大掺量铜矿渣复合粉混凝土分别进行了基本性能试验研究，包
括塑性混凝土性能、硬化混凝土力学性能和耐久性。试验结果表明，大掺量铜矿渣复合粉混凝土具有早期强度高、塑
性收缩和干缩低、耐久性好等特点。
关键词：普通混凝土；大掺量矿渣粉混凝土；大掺量铜矿渣复合粉混凝土；力学性能；耐久性
Abstract：The basic properties of ordinary concrete，concrete mixed with a large amount of slag power and concrete
mixed with a large amount of steel slag composite powder are studied including the plastic properties of concrete，the me—
chanical properties and durability of hardened concrete．The test results show that the concrete mixed with a large amount
of steel slag composite powder has good technical characteristics，such as high early strength，low plastic shrinkage and dry
shrinkage，good durability．
Key words：Ordinary concrete；Concrete mixed with a large amount of slag power；Concrete mixed with a 1arge
amount of steel slag composite powder；Technical characteristics；Durability
中图分类号：TU528 文献标识码：A 文章编号：1000—4637(2015)02—89—04
0 前言
近年来。随着GB／T 18046—2008(用于水泥和混
凝土中的粒化高炉矿渣粉》标准的出台，以及国内
钢铁厂矿渣粉生产线的陆续投产，矿渣粉和粉煤灰
双掺技术已经普遍被预拌混凝土企业所采用，但矿
渣粉和粉煤灰的掺量一般较低，分别占胶凝材料总
量的15％～18％左右，如果进一步提高掺量，将明显
降低}昆凝土的早期强度，影响施工进度，尤其在冬
季施工。大掺量矿渣粉混凝土尽管已在东海大桥、
杭州湾跨海大桥等重大工程中应用，但主要用于生
产蒸养预制构件，在一般工业和民用建筑中仍应用
较少。
另一方面．我国冶炼渣年产生量约为3．15亿t，
其中钢渣0．8亿t，矿渣1．9亿t，冶炼渣的综合利用
率仅为55％，特别是钢渣的利用途径较少，主要用
于工程回填和筑路，附加值较低。国家鼓励“推广生
产钢铁渣复合粉作水泥和混凝土掺合料”{11。因此，
应加快研发钢渣矿渣双掺和大掺量应用技术。
本文以超细钢渣粉和脱硫石膏作为辅助胶凝
材料和激发材料，与矿渣粉复配开发出一种新型钢
矿渣复合粉。与普通混凝土相比，大掺量钢矿渣复
合粉混凝土用于一般工业与民用建筑在技术经济
上具有相当的优势。
1 试验原材料
1．1 主要原材料的化学成分
本文研究的新型钢矿渣复合粉主要由水泥、矿
渣粉、钢渣粉、粉煤灰、脱硫石膏等原材料组成，各
原料的化学成分见表1。
表1 主要原材料的化学组成％
1．2 主要原材料的物理性能
水泥：P·0 42．5级水泥，物理指标性能见表2。
基金项目：上海市科委项目(12DZ0510600)；上海市国资委
项目(2013016)资助。
矿渣粉：$95矿渣粉，物理性能指标见表3。
超细钢渣粉：采用预粉磨、循环除铁、高细磨、
选粉等工艺生产而成，比表面积大于600m~kg，粒径
小于301xm的颗粒含量占90％以上。金属铁含量≤