成型方式对再生混凝土性能影响的试验研究

资料大小：320KB
资料类型：.PDF
资料等级：
发布时间：2021-09-08

资料介绍

成型方式对再生混凝土性能影响的试验研究
田正林。吴相豪
(上海海事大学海洋环境与工程学院，上海201306)
摘要：通过试验研究了真空脱水、净浆裹石和粗骨料预湿三种成型方式对再生粗骨料混凝土抗压强度和抗氯离子渗透
性能的影响。结果表明：(1)随着真空度的增加，再生粗骨料混凝土抗压强度是先增大后减小，最佳真空度为0．06MPa；抗氯离子渗
透陛能是先增强后减弱，最佳真空度为0．04 MPa。(2)净浆裹石对再生粗骨料混凝土抗压强度和抗氯离子渗透眭能有一定的影响。用
水泥和75％的水拌制的净浆裹石能明显提高再生粗骨料混凝土的抗压强度；用水泥和50％的水拌制的净浆裹石能明显改善再生粗
骨料混凝土的抗氯离子渗透性能。(3)再生粗骨料混凝土抗压强度随着预湿再生粗骨料水量的增加而增大；抗氯离子渗透能力随着
预湿再生粗骨料水量的增加是先增强后减弱，最佳预湿用水量为配合比水量的3％。
关键词：再生混凝土；真空脱水；净浆裹石；粗骨料预湿；抗压强度；氯离子渗透
中图分类号： TU528．063 文献标志码： A 文章编号： 1002—3550(2014)07—0145—04
Experimental research of forming technology efects on properties of recycled concrete
TIANZhenglin，W UXianghao
(College ofOceanEnvironment andEngineering，ShanghaiMaritimeUniversity，Shanghai 201306，China)
Abstract： The effects of three forming technologies，vacuum dewatering，interfacing stone enveloped with cement and coarse aggregate
pre—wet，on compressive strength and chloride ion penetration of recycled coarse aggregate concrete arc researched by experiments．Results
show that：1)The compressive strength ofrecycled coarse aggregate concrete first increases and then decreases with the increase ofthe vac—
uum degree，the best vacuum degree is 0．06 M Pa，the chloride ion penetration of recycled coarse aggregate concrete is enhanced firstly and
then weakened with the best vacuum degree of 0．04 MPa．2、Interfacing stone enveloped with cement has certain effects on compressive
strength and resistance to chloride ion permeability of recycled coarse aggregate concrete．Interfacing stone enveloped with cement result
shows that with75％ water Call significantly increase the compressive strength ofrecycled coarse aggregate concrete；however，interfacing
stone enveloped with cement with 50％ water can improve the recycled coarse aggregate concrete resistance to chloride ion penetration sig—
nificantly．3)With the increase ofthe amount ofcoarse aggregate pre—wet water，the compressive strength ofrecycled coarse aggregate con—
crete increases and the resistance to chloride ion penetration capacity increases firstly and then decreases，the best amount of coarse aggre—
gate pre—wet water is 3％ ofmixing ratio water．
Key w ords： recycled concrete；vacuum dewatering treatment；interface stone enveloped with cement；coarse aggregate pre·-wet；corn--
pressive strength；chloride ion penetration
0 引言
混凝土的物理力学性能除了与组成混凝土的材料品
质、材料配合比、养护条件有关外，还与混凝土的成型方式
等因素有关。文献[1—2]研究了真空脱水对混凝土抗压强度
和抗氯离子渗透性能的影响，真空脱水能使混凝土的抗压
强度增加10％至20％，氯离子含量降低约20％。文献[3—4]
的研究表明，净浆裹石可以提高混凝土的抗压强度和耐久
性能。文献[5—7]研究了页岩陶粒经不同程度预湿处理后轻
集料混凝土强度和抗冻性的变化规律。这些研究成果主要
集中在普通混凝土和轻骨料混凝土，有关混凝土成型方式
影响再生混凝土物理力学性能的研究成果较少。为此，笔
者通过室内试验研究了真空脱水、净浆裹石和粗骨料预湿
三种成型方式对再生粗骨料混凝土抗压强度和氯离子渗
透性能的影响规律。
1 试验
1．1 原材料及配合比
水泥：海螺牌P·O 42．5水泥。细骨料：细度模数为
2．82的河砂。粗骨料：废弃混凝土经过清洗、破碎、筛分后
得到的粒径为5~40 mm的再生骨料，含水率为0．3％。水：
自来水。