超细粉煤灰高性能混凝土耐久性试验研究
Study on Durability of High Performance Concrete Containing Ultra-Fine Fly Ash
孙鑫鹏，李益进。尹健
(中南大学土木建筑学院，湖南长沙410075)
摘要：研究了由电收尘气流分选工艺收集的超细粉堞灰(UFA)对高性能混凝土耐久性能的影响。结果表明：超细粉煤灰提
高了高性能混凝土的抗冻性和抗渗性，掺UFAI(适用于C50一C70的高温性能混凝土工程的超细粉煤灰)的高性能
混凝土其单位面积磨损量均有不同程度的降低并具有优良的护筋性，掺粉煤灰可以改善高性能混凝土的抗硫酸盐侵蚀
性，尤其是对混凝土的早期强度和干缩性能具有显著的改善效果。
关键词：粉煤灰；高性能混凝土；耐久性
中图分类号：TU528．31 文献标识码：A
Abstract：This paper focuses on the influence of ultra—fine fly ash，which was collected by electro·static preeipitators and with
airflow classification technology，on the durability of HPC．The experimental results indicate the addition of UFA improves the
frost resistance of concrete and impermeability，per unit area wear extent of high—performance concrete mixed with UFAI has
reduced in different degree and it also has excellent bars security,otherwise，fly ash can improve the sulfate attack resistance of
high performance concrete，especially have a significant improvement on the early strength and dry shrinkage performance of concrete．
Key words：ultra-fine fly ash；high performance concrete；durability
0前言
高性能混凝土是通过掺磨细活性混合材和高效复合外
加剂等来达到混凝土硬化前和硬化后具有优异性能的混凝
土。这些性能主要包括：高流动性、高抗离析性、低塌落
度损失和高耐久性等。粉煤灰高性能混凝土出色地具备高
抗渗性、强耐腐蚀性并能克服本身的内部病态，是实现粉
煤灰资源化、商品化和综合社会效益一体化的一条重要途
径。
当前国内粉煤灰的利用开发很不平衡，经济发达地区
如上海、广州、深圳等地粉煤灰有供不应求之势，而有些
地区粉煤灰的利用率仅为25％左右，甚至更低。
本文研究了由电收尘气流分选工艺收集的超细粉煤灰
及复合超细粉煤灰，等量取代水泥25％ 40％，作为混凝
土的第六基本组成材料，配制出粉煤灰高性能混凝土和实
现普通混凝土的高性能化，符合我国材料可持续发展的国
策。在试验室研究的基础上，从工程实践应用的角度论证
了超细粉煤灰的掺量对高性能混凝土的长期性能及耐久性
能的影响，对粉煤灰高性能混凝土在钢筋混凝土桥梁、路
面、大体积混凝土以及快速重铺混凝土路面的推广应用具
14 CoAL ASH 1／2010
有重要意义。
1原材料及试验方法
1．1原材料
水泥：韶峰牌42～级普通硅酸盐水泥，实测28 d抗
压强度为53—57 MPa；
砂：湘江河砂，级配合格的Ⅱ区砂，细度模数为2．88；
石：5 20 mm的石灰岩碎石及碎卵石，级配合格，
碎石压碎指标为7．60％一8．60％；碎卵石系指将大于最大
粒径的湘江河卵石轧碎而成碎卵石混和体，其中碎石占
51％ 53％，压碎指标7．70％～8．00％；
超细粉煤灰矿物外加剂：湘潭电力粉煤灰开发有限责
任公司生产，比表面积为620 m ／kg；
高效减水剂：萘系高效复合减水剂。
表1 超细粉煤灰(UFA)的化学组成和性能