超轻EPS复合泡沫混凝土性能研究
杨奉源，卢忠远，何顺爱，牛云辉
(西南科技大学I~tJ Jl省非金属复合与功能材料重点试验室一省部共建
国家重点试验室培育基地，绵阳621010)
摘要：通过向低水灰比高流动性水泥浆中掺入不同比例的泡沫和EPS颗粒，制备了一系列200 kg／m3超轻
EPS复合泡沫混凝土，并测试了强度、吸水率、软化系数、干缩、导热系数等性能。结果表明，EPS颗粒的引入可以提
高复合体系的强度，降低吸水率，提高软化系数，降低干缩，不会明显影响导热系数，表明EPS可作为制备超轻泡沫
混凝土的优质填充料。
关键词：EPS；泡沫混凝土；强度；吸水率；软化系数；干缩
Abstract：A series di rent ratios of foam and EPS particles has been added to the low water cement ratio paste with
high fluidity to prepare a series of 200 kg／m。uhra lightweight EPS foam concrete．The strength，water absorption rate，soft—
ening coeficient，drying shrinkage and thermal conductivity of the EPS foam concrete have been tested．It has been ob—
served that the addition of EPS particles can improve the strength and softening coeficient，reduced water absorption rate
and drying shrinkage，and not significantly affect the thermal conductivity of the composite system，which indicates that
EPS could be used as a high-quality filler for preparing ultra lightweight foam concrete．
Key wor~ ：EPS；Foam concrete；Strength；Water absorption rate；Softening coeficient；Drying shrinkage
中图分类号：TU528．2 文献标识码：A 文章编号：1000—4637(2012)05—09—04
0 前言
泡沫混凝土是通过向水泥浆料中引入预先用
发泡液通过物理方式制备的泡沫后制成的气泡均
匀分布的水泥基多孔材料。泡沫混凝土的密度通常
在400-1600k~m ，具有隔热、隔音、轻质、调湿、吸
能、吸声、可泵送现浇等多种特性，现已成为建筑节
能减排领域的研究热点，广泛应用在地暖绝热层、
屋顶绝热层、墙体自保温、回填工程等方面【 -2]。
超轻泡沫混凝土是指密度小于300k~m 的泡
沫混凝土，国内外相关研究文献不多，基本研究数
据见表1。由表1可知，导热系数因测试方法和孔特
性不同而有一定的差异，但均表明超轻泡沫混凝土
具有良好的隔热效果。国外研究中的试件强度普遍
较低，而国内研究者采用了双快水泥，凝结快、强度
高，但凝结时间过短不利于泵送现浇。
目前，关于EPS复合泡沫混凝土(后文简称为
EPS—FC)的研究[9-“1多为密度较高的EPS复合体系，
仅有Laukaitis等『l21研究了EPS颗粒种类及掺量对
基金项目：西南科技大学研究生创新基金项目(1lycjj08)、国
家科技支撑计划项目(201 1BAE14B05)。
140～320k~m EPS—FC强度、弹性模量、导热系数的
影响，结果表明，采用回收破碎得到的EPS颗粒所
制备的150-170k~m。密度EPS—FC，导热系数为
0．06-0．064W／(m·K)，强度可达0．25-0．28MPa。然而，
其研究中所用的基体泡沫混凝土密度仅一种，约为
600k#m。，没有考虑泡沫混凝土密度对EPS—FC强
度的影响，也没有研究其他方面的性能。
表1 超轻泡沫混凝土相关研究文献数据
因此，本文拟通过向低水灰比高流动性水泥浆
中掺人不同比例的泡沫和EPS颗粒，制备一系列不
同密度泡沫混凝土与EPS颗粒复合的200k#m 超
轻EPS—FC，以期改善泡沫混凝土的性能，拓展此类