掺石灰粉对粉煤灰再生混凝土抗冻性能的影响
Influence of Lime Powder on Freezing—Thawing Performance of
Fly Ash Recycled Concrete
朱涛，吴相豪，袁潘
(上海海事大学海洋环境与工程学院，上海201306)
摘要：采用快速冻融试验方法，研究了石灰粉掺量对粉煤灰再生混凝土抗冻性能的影响规律。试验结果表明：
石灰粉等量取代部分粉煤灰对粉煤灰再生混凝土抗冻性能有一定的影响，随着石灰粉等量取代粉煤灰率
的增加，粉煤灰再生混凝土抗冻性能是先增强后减弱，掺适量的石灰粉可以改善粉煤灰再生混凝土的抗
冻性能，石灰粉最佳取代率为10％左右。
关键词：粉煤灰；石灰粉；再生混凝土；抗冻性能
中图分类号：TU528．2 文献标志码：A
Abstract： The influence of lime powder on freezing．thawing performance of fly ash recycled concrete was investigated by
accelerated freezing and thawing test．The results showed that：substituting lime powder for part of isometric fly ash has a certain
influence on the frost resistance of fly ash recycled concrete．frost resistance of recycled concrete increased firstly and then
decreased with the ratio of lime powder raising，thence，an appropriate amount of lime powder could improve the frost resistance
of recycled concrete．the optimum replacement ratio iS about 1 O％．
Kev words：fly ash；lime dust；recycled concrete：freezing and thawing
0 前言
在寒冷地区，冻融是主要的环境荷载，是引起混凝土
结构破坏的主要因素。抗冻性能是评价混凝土结构耐久性
的重要指标之-[1-3]。再生混凝土是一种环保型建筑材料，
越来越多地应用于建筑工程领域，有必要开展再生混凝土
抗冻性能的研究。冯嘉等[ 1等研究了矿物掺合料等因素对
再生混凝土抗冻性能的影响，结果表明掺普通矿粉的再
生混凝土比掺粉煤灰的再生混凝土抗冻性好，硅灰对提高
再生混凝土抗冻性有明显作用。王军强等【】研究了再生混
凝土的基本力学性能和抗冻耐久性能，结果表明采取外
掺粉煤灰和引气剂配置的再生混凝土具有较强的抗冻性能，
可以满足寒冷区域环境下使用。理论上讲，石灰是一种以
氧化钙为主要成分的气硬性无机胶凝材料，具有一定的活
性，加入粉煤灰再生混凝土拌合物中，可增加粉煤灰再生
混凝土中的含量，提高粉煤灰的活性，从而改善再生混凝
土的性能。因此，本文拟研究双掺粉煤灰和石灰粉对再生
混凝土抗冻性能的影响规律。
40 CoAL AsH 1／2013
1 试验
1．1 原材料及配合比
1．1．1 原材料
水泥：P．O 42．5海螺牌水泥。粉煤灰：Ⅱ级粉煤灰，
45 m筛的筛余为l4．8％，需水量比为98．6％，烧失量为
5．79％。石灰粉：上海金山生产的生石灰，在室内空气中
自然熟化而成的粉末，用25 m方孔筛过筛，取粉末装
入防潮塑料瓶备用(有效钙含量≥85％)。再生粗集料：
选用路面废弃混凝土，人工破碎后，再除杂、筛选、分级、
清洗得到粒径在5～20 mm范围的粗集料。细集料：选用
细度模数为2．82的河砂。水：采用自来水。
1．1．2 配合比
试验采用100％的再生粗集料，水胶比为0．55。双掺
粉煤灰和石灰粉时，水泥用量固定为胶凝材料用量的60％，
石灰粉的掺量分别为胶凝材料用量的0、4％、8％和12％。
由于现行规范还未给出再生混凝土配合比的设计方法，试
验按普通混凝土设计规程进行配合比设计，粉煤灰再生混