掺锂渣再生粗骨料混凝土抗压强度试验研究

资料大小：350KB
资料类型：.PDF
资料等级：
发布时间：2021-09-07

资料介绍

掺锂渣再生粗骨料混凝土抗压强度试验研究
于江，严文龙，秦拥军，罗玲
(新疆大学建筑工程学院，乌鲁木齐830047)
摘要：锂渣及再生粗骨料对混凝土抗压强度有一定的影响，通过轴心抗压试验获得了立方体与棱柱体抗压强
度之间的线性关系。结果表明，适量的再生粗骨料和锂渣可以有效提高混凝土28d抗压强度，当再生粗骨料取代率
为30％，锂渣掺量为20％时，28d的立方体和棱柱体抗压强度最大，较同龄期下未掺锂渣的普通混凝土增长了39．1％
和48．2％。
关键词：锂渣；再生粗骨料；立方体抗压强度；棱柱体抗压强度
Abstract：Lithium stag and recycled coarse aggregates have a certain influence on the compressive strength of con—
crete，thmu【gh the axial compressive test，the linear relationship of compressive strength between the cube and prism were
obtained．rrhe results show that the right amount of recycled coarse aggregate and lithium slag can efectively improve the
28d compressive strength．When the replacement rate of recycled coarse aggregate is 30％ and the lithium slag content is
20％，the 28d compressive strength of cube and prism is the largest，is increased b．y 39．1％ and 48．2％ than the compres—
sive strength of the ordinary concrete which is not added by lithium slag in the same age period．
Key words：Lithium slag；Recycled coarse aggregate；Compressive strength of cube；Compressive strength of prism
中图分类号：TU528．041 文献标识码：A 文章编号：1000—4637(2015)08—94一O5
0 前言
目前，国内外已对再生粗骨料混凝土的抗压性
能进行了大量研究。再生粗骨料自身的缺陷造成其
强度不高【，一定程度上限制了再生粗骨料混凝土
的推广和应用。为了弥补其在强度上的不足．将锂
渣作为掺合料加人混凝土中，以期改善混凝土的抗
压性能，从而为实际应用打下基础。
锂渣作为新疆规模化排放的固体工业废弃物，
是利用锂辉石生产碳酸锂过程中排放出来的。通过
硫酸浸渍以提高锂元素的采取量而使得排放出来
的锂渣水分大，酸度大，烘干难度也较大，且烘干后
易起灰扬尘．对环境的污染较大[4]。若把锂渣掺人混
凝土中。既能有效减少其堆存数量，又对混凝土的
力学性能有一定的提高作用[5-6]。但目前国内外尚无
对掺锂渣再生粗骨料混凝土这种新型结构材料进
行系统的探索。
基于再生粗骨料混凝土的研究现状及新疆地
区特点，本文通过测定立方体及棱柱体的抗压强度
来分析影响掺锂渣再生粗骨料混凝土抗压性能的
因素。
1 试验概况
1．1 试验材料
水泥：采用P·0 42．5级普通硅酸盐水泥，化学
成分见表1。
锂渣：来自乌鲁木齐市锂盐厂堆存的固体工业
废弃物，其化学成分如表1所示。