掺锂渣C50高性能混凝土的力学与徐变性能
刘来宝
(I~l JlI省非金属复合与功能材料重点实验室一省部共建国家重点实验室培育基地，
西南科技大学，绵阳621010)
摘要：以12％的锂渣超量取代水泥配制C50高性能混凝土，并测试了混凝土的力学与徐变性能及其随养护龄
期的变化规律。试验结果表明，锂渣的掺入，未对混凝土早期力学性能产生负面影响，而后期强度还较未掺试样有一
定程度的提高；掺锂渣混凝土的徐变变形在加载的初始7d内变化较快，180d以后基本趋于稳定，各龄期皆小于未
掺试样。
关键词：锂渣；混凝土；力学性能；徐变性能
Abstract：C50 high performance concrete by replacing cement with 12％ lithium slag is prepared，and the mechanical
and creeping properties of concrete and the change law of the behaviors with the curing time are tested．The experimental
results show that there is no negative effects on the early age mechanical behavior of the concrete by adding into lithium
slag and the mechanical strength has been improved at the later age compared with the one without lithium slag．The
creeping deform ation of lithium slag concrete changes a lot in 7 days but mostly levels of after 180 days，and the data of
creeping behaviors of all curing ages are less than that of the concrete without lithium slag．
Key words：Lithium slag；Concrete；Mechanical property；Creeping property
中图分类号：TU528 文献标识码：A 文章编号：1000-4637(2012)01-67-03
0 前言
普通混凝土粗骨料与水泥石之间的界面上积
滞着大量的Ca(OH)：，其在界面上的结晶和定向排
列是混凝土强度和耐久性低的主要原因之一。磨细
活性矿物掺合料的掺入可充分发挥其形态效应、填
充效应和火山灰效应，改变混凝土内部的孔结构，
提高密实度，从而使其耐久性提高[1]。随着锂盐工业
快速发展，我国锂渣的排放量与日俱增，由于锂渣
含有较高硅、铝等活性组分和较佳的易磨性，作为
掺合料在混凝土中应用已有一些实例，如四川I明珠
电力公司的金华电航桥工程和德阳八角水泥厂等。
用于金华发电站大坝工程时，锂渣是作为增强抗渗
混凝土添加剂应用的，在八角水泥厂是作为生产高
标号水泥添加剂应用的[2-5]。因此，进一步研究锂渣
对混凝土力学和耐久性能的影响具现实意义。
1 试验材料与方法
1．1 原材料
采用P·O 42．5R型硅酸盐水泥；某锂业公司排
放的露天堆放废弃锂渣(LS)，密度2．41，颗粒级配
见表1；玄武岩碎石，粒径4．75～9．5 mm和4．75～31．5
mm，含泥量1．1％；河砂，细度模数Mx=2．6，含泥量
1．3％；福州某公司产XD一2型高效缓凝减水剂。胶凝
材料的化学组成见表2。