掺粉煤灰混凝土的碳化及抗冻性能试验研究
Experimental Study of Carbonization and Frost Resistance of Concrete Mixed with Fly Ash
杨华美，杨华全，王迎春，严建军
(长江水利委员会长江科学院，水利部水工程安全与病害防治工程技术研究中心，湖北武汉430010)
摘要：研究了不同水胶比、不同粉煤灰掺量混凝土的碳化及抗冻性能。试验结果表明，随着水胶比和粉煤灰掺量的增加，混
凝土碳化深度增加，混凝土碳化深度按方程D=K·tb回归，相关系数大于0．95；碳化深度与粉煤灰掺量及水胶比二元
线性回归较好，混凝土抗压强度越高，抗碳化性能越好。水胶比是影响混凝土抗冻性能的主要因素，粉煤灰对混凝土
抗冻性能具有不良影响。
关键词：混凝土；碳化；抗冻性能；回归
中图分类号：TU528．5 文献标识码：A
Abstract：Carbonization and frost resistance performance of concrete with different water—binder ratio and fly ash content was
studied．Results show that the carbonization depth of concrete increased with increment of water-binder ratio and fly ash content．
The fitting correlation coefficients of concrete carbonization depth with age were high than O．95 by regression equation D K．t”．
The relationship of concrete carbonization depth with fly ash content and water—binder ratio was described well by binary linear
regression equation．Higher concrete compressive strength，better concrete carbonization resistance．The water-binder ratio was
the primary factor influencing frost resistance of concrete，while fly ash in concrete was bad for concrete frost resistance．
Keywords：concrete carbonization frost resistance regression
0概述
混凝土在使用过程中，空气中二氧化碳(CO )不断
向混凝土内部的孔隙和毛细管中渗透，与水泥水化过程中
产生的氢氧化钙(Ca(OH)z)发生化学反应，生成碳酸钙
(CaCO )的作用称为混凝土碳化。混凝土碳化不仅会加
大不可逆收缩川，导致混凝土开裂，同时会导致孔隙中液
相的pH值降低，当混凝土碳化厚度达到钢筋表面时，就要
破坏在高碱环境中钢筋表面产生的钝化膜保护层，使钢筋
粉煤灰可改善混凝土的某些性能，如降低水化热、提
高耐硫酸盐侵蚀能力、抑制碱一集料反应等等，但粉煤灰
掺量的增加对混凝土的抗碳化性能和抗冻融能力却有不良
影响，且粉煤灰对混凝土碳化性能影响尚具争议。。本
文主要探讨了粉煤灰掺量、水胶比对混凝土碳化及抗冻性
能的影响，这对进一步弄清粉煤灰混凝土的碳化机理及抗
冻性能影响规律具有一定的理论意义。
1原材料及试验方法
产生锈蚀Ⅲ。
． 1．1原材料
混凝土受到外界环境不断变化的温度和湿度反复作用
时，混凝土表面会开裂和剥落并逐步深入到内部而导致混
凝土的整体瓦解，并最终丧失其性能，混凝土抵抗这种冻
融破坏的能力称之为抗冻性⋯，抗冻性是评价混凝土耐久
性的一个重要参数。
水泥：水泥为华新水泥股份有限公司生产的42．5中热硅
酸盐水泥，其品质检验结果见表1，检验结果表明，其品
质满足国标《中热硅酸盐水泥，低热硅酸盐水泥，低热矿
渣酸盐水泥》(GB 200—2003)中热水泥的相关要求。