掺粉煤灰、沙漠砂高强混凝土抗压强度研究
陈云龙，马菊荣，刘海峰，宋建夏
(宁夏大学土木与水利工程学院，宁夏银川750021)
摘要：通过正交试验，分析了水胶比、粉煤灰掺量、砂率、沙漠砂取代率对不同龄期高强混凝土抗压强度影响，并给出了配制高强
混凝土的最优配合比。研究结果表明：用沙漠砂替代中砂配制高强混凝土是可行的；综合考虑各阶段的抗压强度，高强混凝土的最优
配合比为水胶比0．24、粉煤灰掺量10％、砂率30％、沙漠砂取代率30％。
关键词：毛乌素沙地砂；粉煤灰；高强混凝土；正交试验
中图分类号： TU528．041 文献标志码： A 文章编号： 1002—3550(2014)07—0080—05
Influence of fly ash and dese~Sand content on the compressive strength of high strength concrete
CHEN Yunlong，MA Jurong，LIU Haifeng，SONGJianxia
(School ofCivil and Hydraulic Engineering，Ningxia University，Yinchuan 750021，China)
Abstract： The onhogonal experiment was designed to analyze the influence of water-binder ratio，fly ash content，san d ratio an d desert
sand replacement ratio on the compressive strength of high strength concrete at the different age．The optimum mix ratio of desert sand
high·strength concrete was also given out．Experimental result showed that it is practical to use the desert sand from Mu Us desert sand to
mix high s~ength concrete，the optimum mix ratio of which was that water—binder ratio，fly ash dosage，san d ratio and desert san d replacemerit
ratio were 0．24，10％，30％ and 30％，respectively．
Key words： Mu Us desert sand；fly ash；high—strength concrete；orthogonal experiment
粉煤灰是我国燃煤电厂排放量最大的固体工业废弃
物之一，是一种灰色粉状废弃物，对环境造成了严重污染。
粉煤灰混凝土是在普通混凝土拌合物中掺加粉煤灰以取
代相同质量或体积的水泥，经常压或高压养护而制成的一
种建筑材料。它不仅能使粉煤灰变废为宝，而且可显著地
改善混凝土的和易性，同时在满足混凝土强度要求下可代
替部分水泥以降低水化热。用粉煤灰取代部分水泥熟料，
不仅可以减少水泥熟料生产量，减少生产水泥对资源的消
耗和CO：排放量，在保护环境、节省资源方面取得很大社
会效益和经济效益。
砂是制备混凝土必不可少的组成之一，我国在经过
大规模基础工程建设后，中、粗砂资源无论从储量、质量
或可持续发展的角度看，都不能满足当今建设规模的需
要，在西北地区分布着大量的沙漠砂资源，从就地取材、
加快施工进度和合理开发利用自然资源的原则出发，利
用丰富的特细砂资源配制混凝土就成为今后工程建设
的必然选择[”。
本研究通过设计正交试验，考虑水胶比、粉煤灰掺量、
砂率和沙漠砂取代率这4个因素，每个因素取3个水平，
分析这些因素对高强混凝土抗压强度的影响，为粉煤灰、
沙漠砂在工程中的应用提供指导和借鉴。
1 试验材料
1．1 水泥
水泥采用宁夏赛马厂生产的强度等级为P·O 42．5R
级的早强水泥。其性能指标如表1所示。
1．2 细骨料
1．2．1 中砂
试验用中砂是产自宁夏镇北堡的人工水洗砂，其物理
性能指标如表2所示，其级配如表3所示。