以废弃混凝土为骨料的二灰碎石的路用性能

资料大小：1M
资料类型：.PDF
资料等级：
发布时间：2021-09-03

资料介绍

以废弃混凝土为骨料的二灰碎石的路用性能
Pavement Performance of Lime-Fly Ash Macadam Using Waste Concrete as
Aggregate
程位
CHENG Heng
陕西高速机械化工程有限公司,陕西西安710038
Shaanxi Expressway Mechanization Engineering Co.Ltd.,Xi'an 710038,Shaanxi,China
【摘要】采用废弃混凝为骨料制作了试件,对以废弃混凝土为再生骨科的二灰碎石的路用性能进行了研究,结果农明:用再生骨料制作的二灰碎石半刚性基层材料显示出良好的力学性能,其无侧限抗压强度、间接抗拉强度和室内
抗压回弹模量等主要力学性能指标完全满足现行规范的要求。
ment performance of macadam was studied. The results indicate that the lime-fly ash macadam shows favorable【Abstract】Waste concrote was applied as aggregate to make specimen of lime-fly ash mecadam,and the pave-
pressive strength,indirect tensile strength and indoor compressive modulus of resilience completely satisfy the mechanics performance when it's applied to semi-rigid base course; main indices such as the unconfined com-
specification.
【关键词】再生骨科;二灰碎石;路用性能:正交试验【Key words Irecycled aggregate;lime-fiy ash macadam; pavement performance;orthogonal test
中图分类号:U416.214 文献标志码:B 文章编号:1000-033X(2012)10-0057-03
0 引言凝材料,其质量的好坏直接影响到二灰碎石混合料的性
能。其中石灰中CaO和MgO的含量对二灰碎石的性能有
近年来,随着国民经济的高速发展,城市建设的速度材料试验规程)(JTJ 058-2000),对消石灰进行了试验,很大的影响。为此,本文按照(公路工程无机结合料稳定
也不断加快,城市里出现了很多建筑垃圾,包括道路翻修
产生的混凝土及房屋拆迁所产生的砖块、混凝土等。对于结果见表1。从表1可以看出,该石灰中有效氧化物的含量
道路建设,这些建筑垃圾都是可再生利用的,有关企业和超过了55%,各项指标均达到了规范中皿级消石灰技术
学者也对此进行了研究。为此,本文结合已有的研究成指标要求,可以用于二灰碎石。
表1 石灰技术指标实测结果
2. 表格
指标
有效COO
含水量细度
(0.71-方孔始第余量)
实测值
61.1
1.36
0.7
规范要求
≥55
64
51
3. 文字
,
侧限抗压强度,间接抗拉强度以及室内回弹模量等常规
力学性能指标出发,研究了以废弃混凝土为再生骨料的
4. 文字
二灰碎石的路用性能,为这种新型二灰碎石的应用提供1.2 粉煤灰
试验数据和理论依据。粉煤灰是火力发电厂排出的废渣,是一种火山灰质
材料,其主要化学成分为SiO,和AL,O,,本试验所选用的粉
1 试验原材料煤灰的主要化学成分和物理性质见表2。从表2可知,该粉
煤灰的技术指标满足《公路路面基层施工技术规范》(JTJ
1.1 石灰 034-2000)对粉煤灰的技术要求,可以用于二灰碎石混
石灰和粉煤灰在道路二灰碎石混合料中共同作为胶合科。